歯科用ブラケット用ZTAセラミックの新規調製法【JST・京大機械翻訳】

Advanced Preparation Method of ZTA Ceramic for Dental Brackets

著者 (5件)： Nie Yuqiang (College of Materials Science and Engineering,North China University of Technology,Hebei Provincial Key Laboratory of Inorganic Nonmetallic Materials) ,  Wang Limei (College of Oral Medicine, North China University of Technology) ,  Xu Jiaxin (College of Materials Science and Engineering,North China University of Technology,Hebei Provincial Key Laboratory of Inorganic Nonmetallic Materials) ,  Chen Yang (College of Materials Science and Engineering,North China University of Technology,Hebei Provincial Key Laboratory of Inorganic Nonmetallic Materials) ,  Qiao Ning (College of Materials Science and Engineering,North China University of Technology,Hebei Provincial Key Laboratory of Inorganic Nonmetallic Materials)
資料名： Zhongguo Taoci  (Zhongguo Taoci)
巻： 52  号： 9  ページ： 69-74  発行年： 2016年 
JST資料番号： C2267A  ISSN： 1001-9642  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 擬(作粘結剤)セラミックを,疑似ベーマイトを用いて調製し,そして,酸化剤として濃HNO_3を用いて,ゲル化法によって調製し,そして,乾燥および焼結によって,歯科用セラミックを調製した。この方法の調製法を研究し,直交試験により最適パラメータを得て,ZRO_2の添加量と焼結温度の影響を研究し,ZRO_2の強靭化機構を論じた。実験結果は以下を示す。ZRO_2含有量と焼結温度は,最終的セラミックの曲げ強さに大きな影響を及ぼし,酸化ジルコニウムの影響は焼結温度よりも大きかった。ZRO_2の含有量が30%と焼結温度が1570°Cのとき,ZTAセラミックの曲げ強さは大きく,同時に,吸水率は歯科用のブラケットの要求に適合した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 粘結剤 ,  吸水率 ,  *歯科学 ,  ベーマイト ,  直交性 ,  曲げ強さ ,  ゲル化 ,  *セラミック ,  酸化ジルコニウム ,  焼結
準シソーラス用語： 強靱化 ,  焼結温度 ,  最適パラメータ , 【Automatic Indexing@JST】