J-GLOBAL ID：201702260297723120   整理番号：17A0061791

冷間圧延後の冷間圧延の影響因子と影響因子の【JST・京大機械翻訳】

Analysis on peeling defects of cold-rolled sheet and its influencing factor

著者 (6件)： Tian Yaqiang (Key Laboratory of the Ministry of Education for Modern Metallurgy Technology,North China University of Science and Technology) ,  Li Ran (Key Laboratory of the Ministry of Education for Modern Metallurgy Technology,North China University of Science and Technology) ,  Song Jinying (Key Laboratory of the Ministry of Education for Modern Metallurgy Technology,North China University of Science and Technology) ,  Zhang Ronghua (Key Laboratory of the Ministry of Education for Modern Metallurgy Technology,North China University of Science and Technology) ,  Zheng Xiaoping (Key Laboratory of the Ministry of Education for Modern Metallurgy Technology,North China University of Science and Technology) ,  Chen Liansheng (Key Laboratory of the Ministry of Education for Modern Metallurgy Technology,North China University of Science and Technology)
資料名： Jinshu Rechuli  (Jinshu Rechuli)
巻： 41  号： 9  ページ： 174-178  発行年： 2016年 
JST資料番号： C2061A  ISSN： 0254-6051  CODEN： JRECDB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 電界放出型走査型電子顕微鏡,エネルギー分散型分光計,および金属顕微鏡を用いて,冷間圧延後の冷間圧延鋼の熱的性質と影響因子を分析した。結果は以下を示す。品質の主な原因は介在物,酸化チャネル,気泡および酸化鉄皮膜圧入である。介在物は主に耐火材と保護材である。酸化チャネルは,主に表面の微小亀裂によって酸化される。気泡は,圧延プロセスの間,板の表面に沿って,最終的に,表面に沿って剥離することができた。大部分の酸化鉄皮膜欠陥の多くは,従来の熱間圧延欠陥による冷間圧延によるものである。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 熱特性 ,  *圧延 ,  分光計 ,  電界放出 ,  熱間圧延 ,  気泡 ,  耐火材料 ,  介在物 ,  走査電子顕微鏡 ,  酸化鉄 ,  *冷間圧延 ,  微小亀裂 ,  酸化 ,  エネルギー散逸
準シソーラス用語： *影響因子 , 【Automatic Indexing@JST】

著者キーワード (6件)： cold-rolled sheet ,  peeling ,  inclusions ,  oxidation pathway ,  bubbles ,  iron oxides

分類 (1件)： 圧延技術  (WC06030Z)

タイトルに関連する用語 (2件)： 冷間圧延 ,  影響因子