焼結磁石の構造と磁気特性に及ぼすAL_2O_3添加の影響を研究した。【JST・京大機械翻訳】

Influence of Al_2O_3 Powder Addition on Microstructure and Magnetic Properties of Sintered Nd-Fe-B Magnets

著者 (7件)： Chen Jinqing (School of Metallurgy and Chemical Engineering,Jiangxi University of Science and Technology) ,  Duan Min (School of Metallurgy and Chemical Engineering,Jiangxi University of Science and Technology) ,  Wu Meihao (Ganzhou Dongci Rare Earth Co. Ltd) ,  Li Longgui (Ganzhou Dongci Rare Earth Co. Ltd) ,  Huang Yaxiang (School of Metallurgy and Chemical Engineering,Jiangxi University of Science and Technology) ,  Huang Bin (School of Metallurgy and Chemical Engineering,Jiangxi University of Science and Technology) ,  Huang Chao (School of Metallurgy and Chemical Engineering,Jiangxi University of Science and Technology)
資料名： Youse Jinshu Gongcheng  (Youse Jinshu Gongcheng)
巻： 6  号： 6  ページ： 1-5,13  発行年： 2016年 
JST資料番号： C2415B  ISSN： 2095-1744  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： (PRND)_(31)(ALCOCUGAZR)_(1.55)B_(0.98)FE合金磁石の密度,微細構造,および磁気特性に及ぼすAL_2O_3添加の影響を研究した。その結果,AL_2O_3粉末の添加量が増加すると,磁石の密度と保磁力は最初増加し,次に減少し,残留磁気と最大磁気エネルギーはゆっくり減少した。AL_2O_3粉末の添加量が0.1%のとき,磁石の密度は0.01G/CM3に増加し,磁石の密度は低下した。AL_2O_3の添加量が0.2%のとき,磁石の保磁力は著しく改善され(5%),磁気的性質は最適化された。微細構造解析の結果,AL_2O_3の適切な添加は磁石の平均粒度を減少させ,磁石の微細構造を改善し,磁石の緻密化を促進することがわかった。さらに,粒界に分布したAL_2O_3/RE_2O_3は,結晶粒を微細化し,結晶粒度を均一にし,結晶粒度を増加させることができた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *磁気的性質 ,  結晶粒界 ,  粉体 ,  最適化 ,  結晶粒 ,  保磁力 ,  粒度 ,  *磁石 ,  精密化 ,  残留磁化 ,  緻密化 ,  微細構造 ,  結晶粒度
準シソーラス用語： 磁気エネルギー ,  *焼結磁石 , 【Automatic Indexing@JST】

著者キーワード (5件)： Al_2O_3 ,  Nd-Fe-B magnet ,  coercivity ,  microstructure ,  magnetic properties

分類 (2件)： 金属結晶の磁性  (BM06040T) ,  電磁石  (NA05080G)

タイトルに関連する用語 (3件)： 焼結磁石 ,  磁気特性 ,  研究