BサイトドープしたNa_0 5Bi_0 5TiO_3ベース鉛フリー強誘電体セラミックの中間温度伝導率【Powered by NICT】

Intermediate-temperature conductivity of B-site doped Na_0.5Bi_0.5TiO₃-based lead-free ferroelectric ceramics

著者 (15件)： Huang Jinqiang (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Huang Jinqiang (Research Institute of Huazhong University of Science and Technology in Shenzhen, Shenzhen 518057, China) ,  Zhu Fangyuan (Shanghai Synchrotron Radiation Facility, Shanghai Institute of Applied Physics, CAS, Shanghai 201204, PR China) ,  Huang Da (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Huang Da (Research Institute of Huazhong University of Science and Technology in Shenzhen, Shenzhen 518057, China) ,  Wang Bing (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Xu Tan (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Li Xiangdong (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Fan Pengyuan (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Fan Pengyuan (Research Institute of Huazhong University of Science and Technology in Shenzhen, Shenzhen 518057, China) ,  Xia Feng (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Xia Feng (Research Institute of Huazhong University of Science and Technology in Shenzhen, Shenzhen 518057, China) ,  Xiao Jianzhong (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Zhang Haibo (College of Materials Science and Engineering, State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Zhang Haibo (Research Institute of Huazhong University of Science and Technology in Shenzhen, Shenzhen 518057, China)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 15  ページ： 16798-16803  発行年： 2016年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Na_0 5Bi_0 5TiO_3(NBT)ベースの酸化物イオン伝導体セラミックスを中温固体酸化物燃料電池(SOFC),酸素センサへの応用に大きな可能性を持っている。xが0,0.01,0.02,0.03,0.05と0.08のNa_0 5Bi_0 0.49Ti_1xMg_xO_3 δセラミックを通常の固相反応により調製した。XRD測定とSEM分析は,二次相を含まない純粋なペロブスカイト構造の形成を明らかにした。MgOドーピングは大幅に焼結温度を低下させ,結晶粒成長を阻害した。ACインピーダンス分光法測定を採用して,全伝導率,MgOドーピング量から0 3mo1%の範囲で増加し,その後減少することが分かったを測定した。空気雰囲気中で600°Cで3mo1%MgOをドープした試料に対して達成された高酸素イオン伝導率σ_t=0.00629/cm。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *ドーピング ,  第二相 ,  *温度伝導率 ,  酸素センサ ,  固相反応 ,  酸化マグネシウム ,  X線回折
準シソーラス用語： イオン伝導率 ,  *伝導率 ,  インピーダンス分光法 ,  焼結温度 ,  ペロブスカイト型構造 ,  中温固体酸化物燃料電池 ,  酸化物イオン伝導体 ,  *強誘電体セラミック , 【Automatic Indexing@JST】

著者キーワード (4件)： Na_0 5Bi_0 5TiO_3 ,  MgOドーピング ,  酸化物イオン伝導率 ,  ACインピーダンス分光法

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： ドープ ,  鉛フリー ,  強誘電体セラミック ,  温度伝導率