低温で水素チャージした急冷超高強度鋼の破壊靭性【Powered by NICT】

Fracture toughness of hydrogen charged as-quenched ultra-high-strength steels at low temperatures

著者 (5件)： Pallaspuro Sakari (Materials and Production Engineering, Centre for Advanced Steels Research, University of Oulu, Finland) ,  Yu Haiyang (Department of Structural Engineering, Faculty of Engineering Science and Technology, NTNU, Norway) ,  Kisko Anna (Materials and Production Engineering, Centre for Advanced Steels Research, University of Oulu, Finland) ,  Porter David (Materials and Production Engineering, Centre for Advanced Steels Research, University of Oulu, Finland) ,  Zhang Zhiliang (Department of Structural Engineering, Faculty of Engineering Science and Technology, NTNU, Norway)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 688  ページ： 190-201  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 遷移温度領域におけるサブゼロ温度での超高強度鋼の破壊および衝撃靭性に及ぼす水素の影響を,北極応用を念頭に置いて研究した。二種類の急冷したままの微細構造は1000MPaに近い降伏強さを持つ,すなわちオートテンパしたマルテンサイトとマルテンサイトとベイナイトの混合物で研究した。これらは受動的陰極防食を用いた水素を充填した,0°C以下の温度での荷電及び非荷電条件の両方で試験した。水素含有量は溶融抽出を用いて測定した。フラクトグラフィー,カーネル平均ミスオリエンテーション測定と融着帯モデリングが,次数と水素脆化の活性機構を考慮して結果を分析した。水素脆化は,0°C以下の温度で存在し,破壊靭性基準温度T_0の増加と変形能のわずかな減少を引き起こすことを示した。,超高強度鋼の場合,低強度鋼で観察されたものから外れた,T_0と衝撃靭性遷移温度T_28Jの間の関係を水素含有量によって影響されることを提案した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 電荷 ,  *水素 ,  マルテンサイト ,  *破壊靱性 ,  *鋼 ,  破面検査 ,  水素脆性 ,  ベイナイト ,  陰極防食 ,  *低温 ,  降伏強さ
準シソーラス用語： ミスオリエンテーション ,  衝撃靱性 ,  遷移温度 ,  *超高強度鋼 , 【Automatic Indexing@JST】

著者キーワード (6件)： 水素脆化 ,  破壊靭性 ,  マルテンサイト ,  サブゼロ ,  凝集域モデル化 ,  カーネル平均方位差

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 低温 ,  水素チャージ ,  急冷 ,  超高強度鋼 ,  破壊靭性