エポキシ被覆した炭素鋼の界面結合強度と安定性に及ぼすZr基化成処理の影響【Powered by NICT】

The influence of a Zr-based conversion treatment on interfacial bonding strength and stability of epoxy coated carbon steel

著者 (5件)： Sababi M. (Materials Innovation Institute (M2i), Elektronicaweg 25, 2628 XG Delft, The Netherlands) ,  Sababi M. (Delft University of Technology, Department of Materials Science and Engineering, Mekelweg 2, 2628 CD Delft, The Netherlands) ,  Terryn H. (Delft University of Technology, Department of Materials Science and Engineering, Mekelweg 2, 2628 CD Delft, The Netherlands) ,  Terryn H. (Vrije Universiteit Brussel, Department of Electrochemical and Surface Engineering, Pleinlaan 2, B-1050 Brussels, Belgium) ,  Mol J.M.C. (Delft University of Technology, Department of Materials Science and Engineering, Mekelweg 2, 2628 CD Delft, The Netherlands)
資料名： Progress in Organic Coatings  (Progress in Organic Coatings)
巻： 105  ページ： 29-36  発行年： 2017年 
JST資料番号： A0541C  ISSN： 0300-9440  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 炭素鋼上の融着エポキシ(FBE)コーティングの界面結合特性に及ぼすジルコニウム(Zr)ベース前処理の影響を調べた。さまざまに前処理した炭素鋼表面に適用したエポキシ皮膜の剥離の開始と速度論を走査Kelvinプローブ(SKP)を用いて研究した。その場減衰全反射Fourier変換赤外分光法(ATR FTIR)を適用して,埋め込まれた界面への電解質拡散に及ぼす界面コーティング酸化物化学の変化を研究することである。対応する塗膜劣化を,電気化学インピーダンス分光法(EIS)を用いて解析した。プルオフ実験は湿潤と腐食条件に曝露したとき特に炭素鋼表面への溶融結合したエポキシコーティングの乾燥及び湿潤接着力特性を改善するZr基前処理の有益な効果を示した。界面結合安定性のこの増加は,ATR-FTIRおよびEIS実験によって確認し,遅延と遅い剥離はSKP測定で観測した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *化成処理 ,  速度論 ,  *界面 ,  湿潤 ,  *付着強さ ,  前処理 ,  *ジルコニウム ,  塗膜 ,  *炭素鋼 ,  付着力
準シソーラス用語： ATR-FTIR分光法 ,  電気化学インピーダンス分光法 ,  減衰全反射 ,  Kelvinプローブ ,  融着 , 【Automatic Indexing@JST】

著者キーワード (6件)： Zr基治療 ,  融解結合エポキシ ,  炭素鋼 ,  界面結合 ,  走査Kelvinプローブ ,  ATR-FTIR

分類 (2件)： 塗料の性質  (YJ03020Q) ,  防食  (WB03040M)

タイトルに関連する用語 (6件)： 炭素鋼 ,  界面 ,  結合強度 ,  安定性 ,  Zr ,  化成処理