サイクル中のLi_2MnO_3陽極材料のSEI膜の組成と変化に関する研究【Powered by NICT】

Study on compositions and changes of SEI film of Li₂MnO₃ positive material during the cycles

著者 (5件)： Cheng Meng (State Key Laboratory of Mechanics and Control of Mechanical Structures, College of Aerospace Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, PR China) ,  Cheng Meng (College of Materials Science and Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China) ,  Tang Weiping (Shanghai Institute of Space Power-Sources, Shanghai 200000, China) ,  Li Yong (Shanghai Institute of Space Power-Sources, Shanghai 200000, China) ,  Zhu Kongjun (State Key Laboratory of Mechanics and Control of Mechanical Structures, College of Aerospace Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, PR China)
資料名： Catalysis Today  (Catalysis Today)
巻： 274  ページ： 116-122  発行年： 2016年10月01日 
JST資料番号： T0363A  ISSN： 0920-5861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Li_2MnO_3電極の表面シリーズとSEI膜の組成の変化を検討した。XPS及びFT-IR分析は,約20at.%LiFを含む一次SEI膜の組成LiFの溶解とLi_xPO_yF_zと有機種の蓄積を含むサイクルにより変化することは,表面腐食が認められた。が有機種は静的腐食によるわずかな変化を示した。不安定不動態膜は高インピーダンスを引き起こし,動的および静的両プロセスにおける電解質腐食を抑制できなかった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 不動態皮膜 ,  インピーダンス ,  電解質 ,  *腐食

著者キーワード (4件)： Li_2MnO_3電極 ,  副反応 ,  SEI膜 ,  表面腐食

分類 (2件)： その他の触媒  (CB06123Z) ,  光化学反応  (CB08020F)

タイトルに関連する用語 (5件)： サイクル ,  陽極材料 ,  SEI ,  組成 ,  研究