CO酸化のためのCu-Mn酸化物の新規合成と形状依存触媒性能【Powered by NICT】

Novel synthesis and shape-dependent catalytic performance of Cu-Mn oxides for CO oxidation

著者 (7件)： Li Zhixun (School of Chemistry and Chemical Engineering, Guangxi University, Nanning 53004, PR China) ,  Wang Honglei (School of Chemistry and Chemical Engineering, Guangxi University, Nanning 53004, PR China) ,  Wu Xingxing (School of Chemistry and Chemical Engineering, Guangxi University, Nanning 53004, PR China) ,  Ye Qinglan (School of Chemistry and Chemical Engineering, Guangxi University, Nanning 53004, PR China) ,  Xu Xuetang (School of Chemistry and Chemical Engineering, Guangxi University, Nanning 53004, PR China) ,  Li Bin (School of Chemistry and Chemical Engineering, Guangxi University, Nanning 53004, PR China) ,  Wang Fan (School of Chemistry and Chemical Engineering, Guangxi University, Nanning 53004, PR China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 403  ページ： 335-341  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 大きな比表面積を有する遷移金属酸化物は,高活性触媒のための魅力的である,多孔性の特徴をもつ遷移金属酸化物の階層構造は,ガス状反応物と生成物の輸送における構造的利点を有している。本研究では,高表面積を有する多孔質Cu-Mn酸化物はアルコール/水溶媒中の低温共沈法,次いで,ポストアニーリングによって得ることに成功した。アルコールの添加は,形状とCO酸化の触媒性能に大きな影響を示した。分裂端をもつダンベル状Cu-Mn酸化物粒子が高い触媒活性を示し,COの完全転化は45°Cで達成され,形状依存触媒活性を示唆した。酸化活性は比表面積,活性表面酸素種とMn(IV)カチオンを含む因子の組み合わせに起因するものであった。結果は高性能Cu-Mn酸化物触媒を設計するための新しい考え方を提供した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 低温 ,  *触媒 ,  酸素 ,  表面積 ,  *触媒活性 ,  共沈 ,  多孔性 ,  比表面積 ,  階層構造 ,  *酸化 ,  *酸化物 ,  *酸化マンガン
準シソーラス用語： 酸化物触媒 ,  遷移金属酸化物 ,  *一酸化炭素酸化 , 【Automatic Indexing@JST】

著者キーワード (4件)： 低温共沈 ,  Cu-Mn酸化物 ,  Catalysis ,  多孔質構造

分類 (2件)： その他の触媒  (CB06123Z) ,  不均一系触媒反応  (CB06100E)

タイトルに関連する用語 (4件)： CO酸化 ,  Cu ,  Mn酸化物 ,  触媒性能