増強CO_2分離のための高亜鉛イオン負荷を持つグラフェンナノシートを組み込んだによる促進輸送膜【Powered by NICT】

Facilitated transport membranes by incorporating graphene nanosheets with high zinc ion loading for enhanced CO₂ separation

著者 (17件)： Peng Dongdong (Key Laboratory for Green Chemical Technology of Ministry of Education, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Peng Dongdong (Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China) ,  Wang Shaofei (Key Laboratory for Green Chemical Technology of Ministry of Education, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Wang Shaofei (Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China) ,  Tian Zhizhang (Key Laboratory for Green Chemical Technology of Ministry of Education, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Tian Zhizhang (Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China) ,  Wu Xingyu (Key Laboratory for Green Chemical Technology of Ministry of Education, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Wu Xingyu (Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China) ,  Wu Yingzhen (Key Laboratory for Green Chemical Technology of Ministry of Education, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Wu Yingzhen (Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China) ,  Wu Hong (Key Laboratory for Green Chemical Technology of Ministry of Education, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Wu Hong (Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China) ,  Xin Qingping (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300072, China) ,  Chen Jianfeng (State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China) ,  Cao Xingzhong (Multi-Discipline Research Division, Institute of High Energy Physics, Chinese Academy of Sciences, Beijing 100049, China) ,  Jiang Zhongyi (Key Laboratory for Green Chemical Technology of Ministry of Education, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Jiang Zhongyi (Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China)
資料名： Journal of Membrane Science  (Journal of Membrane Science)
巻： 522  ページ： 351-362  発行年： 2017年 
JST資料番号： E0669A  ISSN： 0376-7388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,新しい種類の促進輸送膜のポリ(エーテル-block-アミド)(Pebax)マトリックスへの亜鉛イオン修飾グラフェン(GO DA Zn~2+)ナノシートを組み込むことによって調製した。グラフェン酸化物(GO)ナノシートをドーパミン錯体生成反応を利用した亜鉛イオン(Zn~2+)で修飾した。促進輸送膜のCO_2分離特性をモデル系としてCO_2/CH_4混合物を用いて評価した。GO DA Zn~2+ナノシートは膜性能の増強に重要な役割をplaid。最初に,高亜鉛イオン負荷(ナノシートの34.2wt%)は,π錯体生成機構に基づくCO_2の促進輸送を増強し,より高いCO_2透過性と選択性につながった。第二に,高アスペクト比を有するグラフェンナノシートの導入はより曲がりくねったガス輸送チャネルであり,それは大きな分子サイズのCH_4の浸透を妨げ,従ってCO_2/CH_4選択性を高めるのに適したを示した。第三に,ハイブリッド膜の分別自由体積は非常に上昇した,高いCO_2透過性をもたらした。GO DA Zn~2+を取り込んだPebax膜の最適分離特性は137.9BarrerのCO_2透過性と30.6のCO_2/CH_4選択性,元のPebax膜のそれよりも49%と78%高いで達成された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 分子サイズ ,  錯体生成 ,  *グラフェン ,  π錯体 ,  気体輸送 ,  自由体積 ,  チャネル ,  *ナノシート ,  カテコールアミン ,  第一アミン
準シソーラス用語： ハイブリッド膜 ,  高アスペクト比 ,  透過性 ,  生成機構 ,  *促進輸送 ,  *亜鉛イオン , 【Automatic Indexing@JST】

著者キーワード (5件)： 促進輸送膜 ,  ハイブリッド膜 ,  π錯体生成 ,  グラフェンナノシート ,  CO_2分離

分類 (1件)： 膜分離  (XD02120Z)

物質索引 (1件)： ドーパミン

タイトルに関連する用語 (4件)： 増強 ,  亜鉛イオン ,  グラフェンナノシート ,  促進輸送