Al膜におけるほう素格子間原子過飽和固溶体の強化効果【Powered by NICT】

The strengthening effect of boron interstitial supersaturated solid solution on aluminum films

著者 (6件)： Shang Hailong (State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240, China) ,  Shang Hailong (School of Mechanical Engineering, Shanghai Dianji University, Shanghai 200245, China) ,  Ma Bingyang (State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240, China) ,  Shi Kaicheng (State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240, China) ,  Li Rongbin (School of Mechanical Engineering, Shanghai Dianji University, Shanghai 200245, China) ,  Li Geyang (State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240, China)
資料名： Materials Letters  (Materials Letters)
巻： 192  ページ： 104-106  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 様々なレベルB含有量の添加によるアルミニウム-ほう素(Al B)合金膜をAlとBターゲットのマグネトロン共スパッタリングにより合成した。B含有量の強化効果は,微細構造の特性化と膜の微小硬さにより調べた。結果は,B含有量が1.89at%以下のときAl-B膜は単相格子間過飽和固溶体であることを示した。B含有量が0.06at%から1.89at%への添加により,膜の平均粒径は純Alの~100nmから連続的に減少し10nm以下に,膜の微小硬さは3.3GPaから6.0GPaまで連続的に増加した。置換型合金元素(Cr,Fe,Ti,MgおよびCuのような)と比較して,単位当たりのBの強化効果は約十倍大きいことが分かった,これはBの侵入型固溶体による大きな格子歪に起因した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 侵入型固溶体 ,  *ホウ素 ,  合金 ,  格子歪 ,  キャラクタリゼーション ,  *格子間原子 ,  合金元素 ,  マグネトロン ,  スパッタリング ,  微小硬さ ,  *過飽和固溶体 ,  銅 ,  *アルミニウム ,  単相
準シソーラス用語： 同時スパッタリング , 【Automatic Indexing@JST】

著者キーワード (5件)： Al-B合金膜 ,  スパッタリング ,  間質性過飽和固溶体 ,  Microstructure ,  Hardness

分類 (3件)： その他の無機化合物の薄膜  (BK14060A) ,  変態組織,加工組織  (WB01030N) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (5件)： Al膜 ,  ほう素 ,  格子間原子 ,  過飽和固溶体 ,  強化効果