押出法によるハニカムβ-リン酸三カルシウム足場の作製と特性評価【Powered by NICT】

Fabrication and characterization of honeycomb β-tricalcium phosphate scaffolds through an extrusion technique

著者 (6件)： Feng Shenglei (School of Materials Science and Engineering, South China University of Technology, Guangzhou 510641, China) ,  Feng Shenglei (National Engineering Research Center for Tissue Restoration and Reconstruction, Guangzhou 510006, China) ,  He Fupo (School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou 510006, China) ,  Ye Jiandong (School of Materials Science and Engineering, South China University of Technology, Guangzhou 510641, China) ,  Ye Jiandong (National Engineering Research Center for Tissue Restoration and Reconstruction, Guangzhou 510006, China) ,  Ye Jiandong (Key Laboratory of Biomedical Materials of Ministry of Education, South China University of Technology, Guangzhou 510641, China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 9  ページ： 6778-6785  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,初めてハニカムβ-リン酸三カルシウム(β TCP)足場を,押出法によって作製した。ハニカムTCP足場の物理化学的性質と細胞挙動を調べた。結果は,足場が秩序化したチャネル状マクロ孔と一方向相互接続により特徴づけられたことを示した。細孔構造と機械的強度は,押出金型のパラメータを変えることによって調整することができた。足場の細孔径は800μmの範囲であり,一方細孔方向と空隙率に平行な圧縮強度は14から20MPaと60 70%の範囲であった。in vitro細胞挙動,細胞は表面に付着し,足場の内部チャネル状細孔へと成長することを示した;より高い多孔性を有する足場は,良好な細胞増殖不良細胞分化を示した。押出法により作製したハニカム足場は骨組織工学のための有望な候補である。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *細孔 ,  細孔構造 ,  空隙率 ,  チャネル ,  細胞増殖 ,  機械的強度 ,  圧縮強さ ,  細胞分化 ,  細孔径 ,  in vitro実験
準シソーラス用語： *リン酸三カルシウム ,  骨組織工学 ,  細胞挙動 ,  物理化学的性質 ,  *β-リン酸三カルシウム , 【Automatic Indexing@JST】

著者キーワード (6件)： β-リン酸三カルシウム ,  の足場となる ,  押出技術 ,  Interconnectivity ,  ハニカムセラミック ,  細胞挙動

分類 (1件)： 医用素材  (GA05040H)

タイトルに関連する用語 (5件)： 押出法 ,  β-リン酸三カルシウム ,  足場 ,  作製 ,  特性評価