薄膜の高分子凝集体表面特性に及ぼす低温プラズマの影響を研究した。【JST・京大機械翻訳】

Surface characteristics of polymer film treated by oxygen or nitrogen plasma

著者 (7件)： WEI Jianhua (Department of Oral and Maxillofacial Surgery, School of Stomatology, The Fourth Military Medical University) ,  Masao YOSHINARI (Department of Dental Materials Science Tokyo Dental College, 1 -2 -2 Masago Mihama -ku) ,  MA Wei (Oral Implantation Center, School of Stomatology, The Fourth Military Medical University) ,  ZHANG Junrui (Department of Oral and Maxillofacial Surgery, School of Stomatology, The Fourth Military Medical University) ,  FENG Xinghua (Department of Oral and Maxillofacial Surgery, School of Stomatology, The Fourth Military Medical University) ,  Liu Baolin (Oral Implantation Center, School of Stomatology, The Fourth Military Medical University) ,  Yutaka ODA (Department of Dental Materials Science Tokyo Dental College, 1 -2 -2 Masago Mihama -ku)
資料名： Shiyong Kouqiang Yixue Zazhi  (Shiyong Kouqiang Yixue Zazhi)
巻： 24  号： 4  ページ： 525-528  発行年： 2008年07月 
JST資料番号： W1480A  ISSN： 1001-3733  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 目的;酸素(シリルエーテル)の表面特性に及ぼす酸素プラズマの影響を研究した。方法;円形膜の表面上に6膜を形成するために,プラズマ膜法を用いて,低温の表面上の濡れ性,粗さ,および表面形態に及ぼす異なる衝撃時間の影響を測定した。表面基組成の変化をXPSで測定した。【結果】;6膜の重合体表面は,およびの低温プラズマ処理後に,衝撃時間の延長に伴い,表面の接触角が著しく低下し,XPSの結果,O/C比が著しく上昇し,COOH基が増加することを示した。結論;酸素と窒素プラズマは,6膜の表面親水基の含有量を著しく増加させ,表面湿潤性を著しく増加させた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 表面粗さ ,  接触角 ,  *プラズマ ,  酸素 ,  *低温 ,  *分子集合体 ,  衝撃 ,  濡れ ,  *表面性状 ,  重合体 ,  吸湿性
準シソーラス用語： 窒素プラズマ ,  表面形態 ,  酸素プラズマ ,  *低温プラズマ , 【Automatic Indexing@JST】

著者キーワード (4件)： Surface characteristics ,  Plasma-polymerized polymer ,  Contact angle ,  Plasma treatment

分類 (3件)： 表面処理  (YH04112X) ,  プラズマ応用  (BJ02110K) ,  高分子固体のその他の性質  (CG02025L)

タイトルに関連する用語 (5件)： 薄膜 ,  分子凝集体 ,  表面特性 ,  低温プラズマ ,  研究