修飾したPVA/アラビアゴム複合体からなる新しい逆浸透膜生物汚損緩和と塩素抵抗性増大【Powered by NICT】

Novel reverse osmosis membranes composed of modified PVA/Gum Arabic conjugates: Biofouling mitigation and chlorine resistance enhancement

著者 (6件)： Falath Wail (School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA 30332, USA) ,  Falath Wail (Department of Mechanical Engineering, King Fahd University of Petroleum & Minerals, Dhahran 31261, Saudi Arabia) ,  Sabir Aneela (School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA 30332, USA) ,  Sabir Aneela (Department of Polymer Engineering and Technology, University of the Punjab, Lahore, 54590 Pakistan) ,  Jacob Karl I. (School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA 30332, USA) ,  Jacob Karl I. (G.W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, GA 30332, USA)
資料名： Carbohydrate Polymers  (Carbohydrate Polymers)
巻： 155  ページ： 28-39  発行年： 2017年 
JST資料番号： E0961A  ISSN： 0144-8617  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 優れた性能と特徴を用いたアラビアゴム(GA)と結合した新規な架橋ポリ(ビニルアルコール)(PVA)逆浸透(RO)薄膜は,水脱塩のために合成した。RO膜脱塩パラメータ,親水性,表面粗さ,水透過性,塩排除,塩素耐性と生物汚損抵抗のようなデッドエンドROろ過ユニットを用いて評価した。Pluronic F127の取込とアラビアゴムの結合は膜の全体的なRO性能を改善した。本研究では,0.9wt%のアラビアゴムを含む膜PVA GAは優れた浸透,塩排除,塩素と生物汚損抵抗性と機械的強度を提供したことを示した。本研究から発生する最も注目すべき結果は,全体的なRO性能増強は,基板,内部濃度分極のような基板の使用に関連した負の影響を除去することを使用せずに分離層としてPVA/アラビアゴムを利用しながら達成したことである。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *塩素 ,  *逆浸透膜 ,  脱塩 ,  *アラビアゴム ,  *生物汚損 ,  親水性 ,  機械的強度 ,  緩和現象 ,  透水性 ,  複合体
準シソーラス用語： Pluronic ,  濃度分極 ,  Pluronic F127 , 【Automatic Indexing@JST】

著者キーワード (6件)： ポリ(ビニルアルコール) ,  アラビアゴム ,  Pluronic F127 ,  逆浸透膜 ,  生物汚損 ,  塩素抵抗性

分類 (1件)： 多糖類  (CF10054P)

タイトルに関連する用語 (8件)： 修飾 ,  アラビアゴム ,  複合体 ,  逆浸透膜 ,  生物汚損 ,  緩和 ,  塩素 ,  抵抗性