架橋キトサン被覆硫酸カルシウムホイスカの調製とポリ塩化ビニルのその強化【Powered by NICT】

Preparation of a Crosslinked Chitosan Coated Calcium Sulfate Whisker and Its Reinforcement in Polyvinyl Chloride

著者 (5件)： Cui Jiayang (School of Materials Science and Engineering, East China University of Science and Technology) ,  Cai Yangben (School of Materials Science and Engineering, East China University of Science and Technology) ,  Yuan Wenjin (School of Materials Science and Engineering, East China University of Science and Technology) ,  Lv Zhongfei (School of Materials Science and Engineering, East China University of Science and Technology) ,  Xu Shiai (School of Materials Science and Engineering, East China University of Science and Technology)
資料名： Journal of Materials Science & Technology  (Journal of Materials Science & Technology)
巻： 32  号： 8  ページ： 745-752  発行年： 2016年 
JST資料番号： T0871A  ISSN： 1005-0302  CODEN： JSCTEQ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： グルタルアルデヒド架橋キトサン(GACS)で被覆した硫酸カルシウムホイスカ(CSW)本研究では,ポリ塩化ビニル(PVC)を強化するために調製した。結果は,キトサン(CS)及びグルタルアルデヒド(GA)の両方の最適濃度は0.05wt%であることを示した。修正CSWの12wt%を含むPVC複合材料の引張強さ,衝撃強さ,曲げ弾性率およびビカット軟化温度は純粋なPVCのそれと比較して未改質CSWの12wt%PVC複合材料のそれらと比較し,2.9%,42.4%,27.1%,6.8%,17.5%,40.4%,0.8%と3.8%増加した。動的機械分析結果は,改質されたCSW/PVC複合材料は,非修飾CSW/PVC複合材料と純粋なPVCのそれよりもはるかに高い貯蔵弾性率とガラス転移温度を示すことが分かった。さらに,修飾CSW/PVC複合材料は,高い最速分解温度(T(rpd))およびチャー残渣の良好な熱特性を示した。引張破面の走査型電子顕微鏡像から,改良CSWhas PVCマトリックスとの強い界面接着を示した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 破面 ,  動的機械分析 ,  *ポリ塩化ビニル ,  衝撃強さ ,  走査電子顕微鏡 ,  動弾性係数 ,  熱特性 ,  *硫酸カルシウム ,  ガラス転移点 ,  複合材料 ,  軟化点 ,  *ホイスカ ,  引張強さ ,  *キトサン ,  界面接着性 ,  機械的性質 ,  強度
準シソーラス用語： 界面接着 , 【Automatic Indexing@JST】

著者キーワード (5件)： ポリ塩化ビニル ,  高分子複合材料 ,  表面改質 ,  硫酸カルシウム ,  機械的性質

分類 (2件)： 充填剤,補強材  (YH05030J) ,  性質・試験一般  (YH02010S)

タイトルに関連する用語 (7件)： 架橋 ,  キトサン ,  硫酸カルシウム ,  ホイスカ ,  調製 ,  ポリ塩化ビニル ,  強化