H13鋼のレーザクラッディング被覆の最適化と微細構造特性を研究した。【JST・京大機械翻訳】

Process optimization of Co-based coating on H13 steel by laser cladding and its microstructure and properties

著者 (5件)： Ye Hong (School of Materials Science and Engineering,Chongqing University of Technology, Chongqing Municipal Key Laboratory of Institutions of Higher Education for Mould Technology) ,  Yu Wenxin (School of Materials Science and Engineering,Chongqing University of Technology, Chongqing Municipal Key Laboratory of Institutions of Higher Education for Mould Technology) ,  Lei Linping (School of Materials Science and Engineering,Chongqing University of Technology) ,  Mao Shuang (School of Materials Science and Engineering,Chongqing University of Technology) ,  Tang Chao (School of Materials Science and Engineering,Chongqing University of Technology)
資料名： Jinshu Rechuli  (Jinshu Rechuli)
巻： 41  号： 12  ページ： 117-121  発行年： 2016年 
JST資料番号： C2061A  ISSN： 0254-6051  CODEN： JRECDB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ND:YAGレーザを用いて,H13鋼の表面上にCO基合金被覆を調製し,コーティングの品質に及ぼす走査速度と電流強度の影響を解析し,最適パラメータを決定した。走査型電子顕微鏡(SEM)とX線回折(XRD)を用いて,コーティングの微細構造と相組成を分析した。コーティングの断面硬さと耐摩耗性を,硬度と摩擦摩耗試験機を用いて試験した。結果は以下を示す。レーザ走査速度の増加と電流強度の低下は,COベース合金被覆の熔高と幅を減少させ,穴と亀裂の数を減少させることができた。最適化プロセスパラメータは以下の通りであった。走査速度120MM/分,電流200A。このプロセスは,Γ-COとM_(23)C_6相を含む微細な樹枝状晶と共晶から成り,コーティングの硬度は610HV0.2に達した。耐摩耗性は焼入焼戻しH13鋼の1.32倍である。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *最適化 ,  共晶 ,  硬度 ,  走査電子顕微鏡 ,  耐摩耗性 ,  *レーザクラッディング ,  プロセスパラメータ ,  X線回折 ,  YAGレーザ ,  焼戻 ,  樹枝状結晶 ,  相組成
準シソーラス用語： 最適パラメータ ,  走査速度 ,  *AISIH13 , 【Automatic Indexing@JST】

著者キーワード (5件)： laser cladding ,  Co-based coating ,  H13 steel ,  microstructure ,  properties

分類 (2件)： 機械的性質  (WB02030U) ,  金属の機械的性質  (BL01022T)

タイトルに関連する用語 (6件)： H13鋼 ,  レーザクラッディング ,  最適化 ,  微細 ,  構造特性 ,  研究