Ho~3+/Yb~3+共添加シリカゲルマニウム酸塩ガラスにおける増強された2.0μm発光【Powered by NICT】

Enhanced 2.0μm emission in Ho³⁺/Yb³⁺ co-doped silica-germanate glass

著者 (7件)： Xia Jienan (Liangxin College, China Jiliang University, Hangzhou 310018, PR China) ,  Tian Ying (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, PR China) ,  Li Bingpeng (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, PR China) ,  Zheng Lixia (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, PR China) ,  Jing Xufeng (Institute of Optoelectronic Technology, China Jiliang University, Hangzhou 310018, PR China) ,  Zhang Junjie (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, PR China) ,  Xu Shiqing (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, PR China)
資料名： Infrared Physics & Technology  (Infrared Physics & Technology)
巻： 81  ページ： 17-20  発行年： 2017年 
JST資料番号： H0184A  ISSN： 1350-4495  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： シリカ-ゲンルマニウム酸ガラス中の種々のHo~3+/Yb~3+濃度比の熱的および分光学的特性に関する詳細な研究を表示した。熱特性の測定によれば,ホストガラスは高い転移温度(585°C)並びに大きなΔT(155°C)を有していた。2.0μm蛍光はすべての試料から得ることができる。約2.0μmの最大誘導放出断面積をMcCumber理論で計算したHo~3+の0.56×10~ 20cm~2であった。に加えて,その基礎となる機構は蛍光スペクトルにより解析した。,Ho~3+/Yb~3+共添加シリカゲルマニウム酸塩ガラスの望ましい熱特性と分光特性を2.0μm発光の有望な材料である。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 誘導放出 ,  *発光 ,  熱特性 ,  断面積 ,  *ガラス ,  転移温度 ,  *二酸化ケイ素 ,  蛍光スペクトル ,  蛍光
準シソーラス用語： 分光特性 ,  濃度比 ,  *ゲルマニウム酸塩ガラス , 【Automatic Indexing@JST】

著者キーワード (3件)： 2.0μm発光 ,  熱的性質 ,  Ho~3+/Yb3+を~共ドープシリカゲルマニウム酸塩ガラス

分類 (1件)： 無機化合物のルミネセンス  (BM08093J)

タイトルに関連する用語 (4件)： 共添加 ,  シリカ ,  ゲルマニウム酸塩ガラス ,  増強