アルミナナノ粒子修飾紙の性質に及ぼすKH550の効果に関する研究【Powered by NICT】

Investigation on the effects of KH550 on the properties of alumina nanoparticles modified paper

著者 (5件)： Xiang Min (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing, P.R. China, 400044) ,  Liao Ruijin (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing, P.R. China, 400044) ,  Wang Jiyu (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing, P.R. China, 400044) ,  Liang Ningchuan (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing, P.R. China, 400044) ,  Lv Yandong (Alstom Grid Technology Center Co. Ltd Shanghai 201114 China)
資料名： IEEE Conference Proceedings  (IEEE Conference Proceedings)
巻： 2016  号： ICHVE  ページ： 1-4  発行年： 2016年 
JST資料番号： W2441A  資料種別： 会議録 (C)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 改質セルロース紙の特性に及ぼすナノAl_2O_3の表面処理剤としてKH550の影響を述べた。五群の試料は,それぞれ異なるプロセスにより調製し,これらの試料の性能を比較分析した。液体ドーピング法に基づいて,最大引張強さ,破断伸び率とAC絶縁破壊強度は,それぞれ16.67%,19.82%,17.16%増加し,シランカップリング剤KH550により処理されたナノAl_2O_3表面により改質された絶縁紙の機械的および電気的特性は著しく改善されたことを証明した。結果はまた,液体ドーピング法は従来法よりも優れた示した。Copyright 2017 The Institute of Electrical and Electronics Engineers, Inc. All Rights reserved. Translated from English into Japanese by JST【Powered by NICT】

シソーラス用語： 絶縁紙 ,  表面処理 ,  *アルミナ ,  電気的性質 ,  絶縁耐力 ,  *ナノ粒子 ,  シランカップリング剤 ,  セルロース ,  引張強さ
準シソーラス用語： 破断伸度 ,  ドーピング【薬】 ,  比較分析 , 【Automatic Indexing@JST】