C_f/C SiC MoSi_2複合材料のアブレーション特性:熱水浸透温度の影響【Powered by NICT】

Ablation properties of C_f/C-SiC-MoSi₂ composites: Effects of hydrothermal penetration temperature

著者 (5件)： Cao Liyun (School of Materials Science and Engineering, Shaanxi University of Science and Technology, Xi’an, Shaanxi, 710021, PR China) ,  Bai Zhe (School of Materials Science and Engineering, Shaanxi University of Science and Technology, Xi’an, Shaanxi, 710021, PR China) ,  Huang Jianfeng (School of Materials Science and Engineering, Shaanxi University of Science and Technology, Xi’an, Shaanxi, 710021, PR China) ,  OuYang Haibo (School of Materials Science and Engineering, Shaanxi University of Science and Technology, Xi’an, Shaanxi, 710021, PR China) ,  Wu Jianpeng (School of Materials Science and Engineering, Shaanxi University of Science and Technology, Xi’an, Shaanxi, 710021, PR China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 703  ページ： 45-55  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： C_f/C SiC MoSi_2複合材料のアブレーション特性に及ぼす水熱浸透温度の影響を調べた。水熱温度が上がると,複合材料の断面に沿ってセラミックの分布深さは増加した。一方,密度の増加と複合材料の気孔率の減少が達成された。浸透温度が200°Cに達すると,複合材料は2300°Cで60秒間プラズマアブレーション試験後の最良のアブレーション特性を示した。質量アブレーション速度は2.28mg cm~ 2S~ 1,140°C,160°Cと180°Cで調製した複合材料に比べて65%,54%および29%減少したであった。また,200°Cで作製した試料は最低の線形アブレーション速度を示した。複合材料中のセラミックスの深さの増加と量は炭素の酸化を防ぐためにSiCとMoSi_2continuouslyを提供し,より強い洗掘によって容易にブローすることができた。良好なアブレーション挙動はセラミック,SiO_2とMoO_2の発生のより高い密度と量に起因した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *浸透 ,  線形性 ,  *複合材料 ,  熱浸透 ,  炭素 ,  *アブレーション ,  セラミック ,  洗掘 ,  *熱水 ,  空隙率 ,  *炭化ケイ素

著者キーワード (3件)： C_f/C SiC MoSi_2複合材料 ,  水熱温度 ,  アブレーション性能

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (5件)： SiC ,  複合材料 ,  アブレーション ,  熱水 ,  浸透