循環溶液共蒸着法を用いたNi-SiC複合被覆の電着のための新しいめっき装置【Powered by NICT】

A novel plating apparatus for electrodeposition of Ni-SiC composite coatings using circulating-solution co-deposition technique

著者 (6件)： Zhou Y. (School of Aeronautics, Northwestern Polytechnical University, Xi’an, 710072, PR China) ,  Xie F.Q. (School of Aeronautics, Northwestern Polytechnical University, Xi’an, 710072, PR China) ,  Wu X.Q. (School of Aeronautics, Northwestern Polytechnical University, Xi’an, 710072, PR China) ,  Zhao W.D. (School of Aeronautics, Northwestern Polytechnical University, Xi’an, 710072, PR China) ,  Chen X. (School of Aeronautics, Northwestern Polytechnical University, Xi’an, 710072, PR China) ,  Chen X. (School of Materials Science and Engineering, Northwestern Polytechnical University, Xi’an, 710072, PR China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 699  ページ： 366-377  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 複雑形状円筒のための革新的な複合めっき装置を提案した。電解質中で完全に浸漬しない円筒を可能にした。新しいめっき装置における循環溶液共析出(CSD)法を用いて,Ni-SiC複合被覆は円筒の内面に堆積させることができるが,外遺跡などに異常はなかった。外表面は特異的機能の必要性を満たすために高精度を必要とするエンジンシリンダのための非常に重要であり,電着中の電解質による腐食することができない。Ni被覆のそれと比較して,Ni-SiC被覆の形態,構造,硬度,耐食性と耐摩耗性を解析した。特性化実験により,堆積速度の体積分率は約83μm/30分であることを明らかにした。純Ni被覆と比較して,Ni-SiC複合被覆は良好な耐食性性能,より高い硬度,より大きな摩耗抵抗を示した。Ni-SiCのための支配的な摩耗メカニズムは,アブレシブ摩耗と酸化摩耗である。これらの結果は,CSD法は高い蒸着速度で優れた耐食性と耐摩耗性を持つNi-SiC複合被覆を調製するための効率的な技術であることを証明した。大規模工業化計画のために提案された複合めっき装置は高度に推奨するに値する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 摩耗 ,  耐摩耗性 ,  *電着 ,  *ニッケル ,  複合めっき ,  キャラクタリゼーション ,  アブレシブ摩耗 ,  硬度 ,  *炭化ケイ素 ,  堆積速度 ,  円筒 ,  耐食性 ,  浸漬 ,  *被覆 ,  体積率

著者キーワード (5件)： 電着 ,  循環溶液共析出 ,  Ni-SiC複合材料被覆 ,  装置 ,  耐摩耗性