粉末冶金法によって調製したM2052合金の性質に及ぼす焼結温度の影響を研究した。【JST・京大機械翻訳】

Influence of sintering temperature on properties of M2052 alloy prepared by powder metallurgy

著者 (7件)： Wang Zhubo (State Key Laboratory for Powder Metallurgy, Central South University) ,  Lu Fengshuang (Functional Materials Research Institute, Central Iron and Steel Research Institute, Beijing Key Laboratory of Precision Alloys) ,  Wu Bin (Functional Materials Research Institute, Central Iron and Steel Research Institute, Beijing Key Laboratory of Precision Alloys) ,  Xu Ran (State Key Laboratory for Powder Metallurgy, Central South University) ,  Zhang Jianfu (Functional Materials Research Institute, Central Iron and Steel Research Institute, Beijing Key Laboratory of Precision Alloys) ,  Zhao Dongliang (Functional Materials Research Institute, Central Iron and Steel Research Institute, Beijing Key Laboratory of Precision Alloys) ,  Luo Fenghua (State Key Laboratory for Powder Metallurgy, Central South University)
資料名： Gongneng Cailiao  (Gongneng Cailiao)
巻： 47  号： 9  ページ： 9211-9215  発行年： 2016年 
JST資料番号： C2095A  ISSN： 1001-9731  CODEN： GOCAEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： MN,CU,NI,FE粉末を用い,反応焼結プロセスによりM2052合金を調製した。密度,多孔性,および機械的性質に及ぼす焼結温度の影響を研究し,焼結サンプルの相組成を分析した。950°Cで焼結したM2052合金は,Γ-MNCU固溶体であり,密度は6.23G/CM3,密度は87.2%,曲げ強さは487MPAに達し,良好な減衰特性を示し,異なる周波数での減衰性能は安定していた。損失係数TANΔは0.11~0.12に達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 反応焼結 ,  相組成 ,  *合金 ,  周波数 ,  多孔性 ,  固溶体 ,  抗力係数 ,  機械的性質 ,  曲げ強さ ,  *粉体 ,  *焼結 ,  *粉末冶金 ,  減衰特性
準シソーラス用語： *焼結温度 , 【Automatic Indexing@JST】

著者キーワード (3件)： Mn-Cu alloys ,  damping capacity ,  powder metallurgy