文献

J-GLOBAL ID：201702277805259143   整理番号：17A0174194

Ni基単結晶超合金の高温応力破断異方性【Powered by NICT】

High Temperature Stress Rupture Anisotropy of a Ni-Based Single Crystal Superalloy

著者 (7件)： Wang Guanglei (Superalloy Division, Institute of Metal Research, Chinese Academy of Sciences) ,  Liu Jinlai (Superalloy Division, Institute of Metal Research, Chinese Academy of Sciences) ,  Liu Jide (Superalloy Division, Institute of Metal Research, Chinese Academy of Sciences) ,  Jin Tao (Superalloy Division, Institute of Metal Research, Chinese Academy of Sciences) ,  Sun Xiaofeng (Superalloy Division, Institute of Metal Research, Chinese Academy of Sciences) ,  Sun Xudong (Northeastern University) ,  Hu Zhuangqi (Superalloy Division, Institute of Metal Research, Chinese Academy of Sciences)
資料名： Journal of Materials Science & Technology  (Journal of Materials Science & Technology)
巻： 32  号： 10  ページ： 1003-1007  発行年： 2016年 
JST資料番号： T0871A  ISSN： 1005-0302  CODEN： JSCTEQ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 900°C/445MPaおよび1100°C/100MPaで[001],[011]および[111]方位を持つ第二世代Ni基単結晶(SC)超合金試験片の高温応力破断異方性を調べ,走査電子顕微鏡により観測されたγ/γ′ミクロ組織と各配向試料の透過型電子顕微鏡によって特性化転位配置の発展に注目した。1100°C/100MPaと900°C/445MPaにおいて,単結晶超合金は明白な応力破断異方性挙動を示した。[001]方位の試料は900°C/445MPaで最長の破断寿命を持ち,[111]配向試料は1100°C/100MPaで最良の破断強さを示した。[011]配向試料は,各試験条件で最悪の破断寿命を示したが,1100°C/100MPaでの応力破断特性は改善され,900°C/445MPaと比較して明らかにした。900°C/445MPaで明らかに応力破断異方性は,主に各配向試料における転位の特徴的な運動に起因していた。一方,1100°C/100MPaで,個々の転位配置と共に,各方位のγ/γ′ミクロ組織の進展も見かけの応力破断異方性において重要な役割を果たす。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 走査電子顕微鏡 ,  破断強さ ,  *単結晶 ,  透過型電子顕微鏡 ,  *高温 ,  *超合金 ,  キャラクタリゼーション ,  *異方性 ,  試験片 ,  *ニッケル
準シソーラス用語： 破断寿命 ,  *応力破断 ,  *単結晶超合金 , 【Automatic Indexing@JST】

著者キーワード (5件)： Ni基単結晶超合金 ,  応力破断特性 ,  Anisotropy ,  微細構造特性化 ,  変形機構

分類 (2件)： 機械的性質  (WB02030U) ,  金属材料  (HC06020Z)

タイトルに関連する用語 (4件)： Ni基 ,  単結晶超合金 ,  応力破断 ,  異方性