1CR13鋼包埋粉末のホウ化の性能研究【JST・京大機械翻訳】

Research on Properties of Pack Boronized 1Cr13 Steel

著者 (5件)： Liu Kai (Institute of Materials Science and Chemistry Engineering, Sichuan University of Science and Engineering) ,  Luo Hong (Institute of Materials Science and Chemistry Engineering, Sichuan University of Science and Engineering, Key Laboratory of Material Corrosion and Protection of Sichuan Province) ,  Luo Changsen (Institute of Materials Science and Chemistry Engineering, Sichuan University of Science and Engineering, Key Laboratory of Material Corrosion and Protection of Sichuan Province) ,  Yin Hongwei (Institute of Materials Science and Chemistry Engineering, Sichuan University of Science and Engineering) ,  Lu Zhipeng (Institute of Materials Science and Chemistry Engineering, Sichuan University of Science and Engineering)
資料名： Rejiagong Gongyi  (Rejiagong Gongyi)
巻： 45  号： 14  ページ： 148-150,154  発行年： 2016年 
JST資料番号： C2487A  ISSN： 1001-3814  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 1CR13鋼の微細構造と機械的性質に及ぼす5時間の保持時間の影響を研究した。1CR13鋼の断面形態を走査型電子顕微鏡で観察した。相組成をXRDによって分析した。層の硬さをナノインデンテーションで測定した。結果は以下を示す。その結果,ホウ化ホウ素は,櫛形状を示さず,そして,ホウ化温度が高いとき,ホウ化層中に,ゆるい孔および空孔が存在した。ホウ化層はFE2B相で構成される。異なる温度で5時間保温すると,深さと硬度は温度の上昇とともに増加した。硼化は基質とよく結合した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 櫛形 ,  保持時間 ,  硬度 ,  *ホウ化処理 ,  保温 ,  走査電子顕微鏡 ,  ナノインデンテーション ,  微細構造 ,  基質 ,  相組成 ,  *鋼 ,  ホウ素 ,  機械的性質 ,  X線回折 ,  粉体

著者キーワード (4件)： 1Cr13 steel ,  pack boronizing ,  hardness ,  thickness

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (3件)： 粉末 ,  ホウ化 ,  研究