反応速度論とNa_2CO_3活性化スラグの機械的性質に及ぼすスラグ特性の評価【Powered by NICT】

Evaluation of slag characteristics on the reaction kinetics and mechanical properties of Na₂CO₃ activated slag

著者 (5件)： Yuan B. (Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600 MB Eindhoven, The Netherlands) ,  Yuan B. (State Key Lab of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, PR China) ,  Yu Q.L. (Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600 MB Eindhoven, The Netherlands) ,  Brouwers H.J.H. (Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600 MB Eindhoven, The Netherlands) ,  Brouwers H.J.H. (State Key Lab of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, PR China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 131  ページ： 334-346  発行年： 2017年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： は炭酸ナトリウム活性化スラグ(SCAS)の反応速度論,反応生成物及び機械的性質に及ぼすスラグ特性を評価した。結果は,スラグ粒径を減少させることにより,SCASの強度与え相の析出は劇的に加速できることを示し,反応ピーク(TRRP)に達するまでの時間は86時間から23時間に促進することができ,約34MPaの3d圧縮強度を達成した。ペーストのフレッシュ挙動は,炭酸カルシウムの初期析出に影響され,スラグの粒径を減らした場合gaylussiteの形成も加速された。試料の初期強度発現は,スラグ粒子の粉末度により大きく支配されることを観測したが,長期強度は最初に転換点に到達するまでスラグ粒子の減少と共に増大し,その後減少した。Na_2CO_3活性化スラグの反応速度に及ぼすアルカリ活性剤添加率およびスラグ特性を含む影響因子を検討した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *反応速度 ,  粒径 ,  強度発現 ,  機械的性質 ,  圧縮強さ ,  炭酸ナトリウム ,  高炉スラグ ,  ペースト ,  *反応速度論 ,  反応生成物 ,  炭酸カルシウム ,  *スラグ
準シソーラス用語： 影響因子 ,  長期強度 ,  粉末度 , 【Automatic Indexing@JST】

著者キーワード (5件)： 炭酸ナトリウム ,  地上粒状高炉スラグ ,  繊度 ,  反応速度論 ,  圧縮強さ