カーボン紙/ポリエチレン複合材料の電熱性能研究【JST・京大機械翻訳】

Electrical Heating Properties of Carbon Nanotube Paper/ High-density Polyethylene Composites

著者 (4件)： Tang Ping (Department of Polymer Materials and Engineering, Faculty of Chemical,Environmental and Biological Science and Technology, Dalian University of Technology) ,  Chen Zhiqiang (Department of Polymer Materials and Engineering, Faculty of Chemical,Environmental and Biological Science and Technology, Dalian University of Technology) ,  Hu Yunping (Department of Polymer Materials and Engineering, Faculty of Chemical,Environmental and Biological Science and Technology, Dalian University of Technology) ,  Bin Yuezhen (Department of Polymer Materials and Engineering, Faculty of Chemical,Environmental and Biological Science and Technology, Dalian University of Technology)
資料名： Gao Fenzi Tongbao  (Gao Fenzi Tongbao)
号： 11  ページ： 45-53  発行年： 2016年 
JST資料番号： C2902A  ISSN： 1003-3726  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： カーボンナノチューブ(CNT)の分散性を改良するために,カーボンナノチューブ(CNT)を,高密度ポリエチレン(HDPE)と混合し,そして,高密度ポリエチレン(HDPE)と混合して,サンドイッチ構造を有するCNP/HDPE複合材料を調製した。CNPのモルフォロジー,孔構造,機械的性質,およびCNP/HDPE複合材料の電熱特性を詳細に研究した。結果は以下を示す。懸濁濾過法を用いて,滑らかな表面,滑らかな表面,および均一な孔径を得ることができた。炭素の大部分は,20NM~40NMの範囲に集中していた。Tan納米紙はある程度の強度と柔軟性を有する。複合材料の引張強さと引張弾性率は純粋なHDPEのものよりわずかに高かった。カーボンナノチューブの含有量が同じであるとき,CNP/HDPE複合材料の電気的性質は,同じ電圧の下で,混合方法によって調製したものよりはるかに高かった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 高密度ポリエチレン ,  サンドイッチ構造 ,  柔軟性 ,  カーボンナノチューブ ,  モルフォロジー ,  引張強さ ,  *電気加熱 ,  電気的性質 ,  機械的性質 ,  分散度 ,  電圧 ,  炭素 ,  *複合材料
準シソーラス用語： 引張弾性係数 ,  *カーボン紙 , 【Automatic Indexing@JST】

著者キーワード (4件)： Carbon nanotube paper ,  Electrical heating property ,  Conductive composite ,  Polyethylene

分類 (1件)： 炭素とその化合物  (YB02060D)

タイトルに関連する用語 (5件)： カーボン紙 ,  ポリエチレン ,  複合材料 ,  電熱 ,  研究