CuNiSi合金の高サイクル疲労特性に及ぼす結晶粒度と析出硬化の影響【Powered by NICT】

Influence of grain size and precipitation hardening on high cycle fatigue performance of CuNiSi alloys

著者 (7件)： Gholami M. (TU-Clausthal, Institute of Material Science and Engineering, Clausthal-Zellerfeld, Germany) ,  Vesely J. (Charles University, Department of Physics of Materials, Prague, Czech Republic) ,  Altenberger I. (Wieland-Werke AG, Central Laboratory, Research & Development, Ulm, Germany) ,  Kuhn H.-A. (Wieland-Werke AG, Central Laboratory, Research & Development, Ulm, Germany) ,  Wollmann M. (TU-Clausthal, Institute of Material Science and Engineering, Clausthal-Zellerfeld, Germany) ,  Janecek M. (Charles University, Department of Physics of Materials, Prague, Czech Republic) ,  Wagner L. (TU-Clausthal, Institute of Material Science and Engineering, Clausthal-Zellerfeld, Germany)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 684  ページ： 524-533  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究の目的は,Cu-2.5Ni-0.5Si-0.06Mg合金(CuNi3Si1Mg)の疲労性能に及ぼす結晶粒微細化の影響を調べることであった。結果は,超微細結晶粒(UFG)CuNi3Si1Mgの疲れ強さは粗粒(CG)CuNi3Si1Mgの疲れ強さより約1.6倍高いことを示した。走査型電子顕微鏡(SEM)を用いて破面の詳細な研究は,初期微視組織が疲れ亀裂核形成機構に影響することを示した。CG CuNi3Si1Mgでは,亀裂は活性化したスリップバンドに起因するが,UFG CuNi3Si1Mgでは,亀裂は滑り帯と双晶境界から核形成した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 滑り帯 ,  微結晶 ,  疲れ亀裂 ,  *析出硬化 ,  双晶境界 ,  疲れ強さ ,  *合金 ,  核形成 ,  走査電子顕微鏡 ,  *高サイクル疲れ ,  亀裂 ,  結晶粒微細化 ,  破面 ,  *結晶粒度
準シソーラス用語： 形成機構 , 【Automatic Indexing@JST】

著者キーワード (4件)： 析出物フリーゾーン(PFZ) ,  Cu-5Ni-5Si-0.06Mg合金 ,  CuNi3Si1Mg ,  高サイクル疲労強度

分類 (2件)： 金属材料  (HC05020S) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (3件)： 高サイクル疲労 ,  結晶粒度 ,  析出硬化