CU/P複合材料の発光と摩擦特性に及ぼす表面被覆の影響を研究した。【JST・京大機械翻訳】

Enhanced Luminescence and Wear Resistance of Copper Matrix Phosphorescent Composite with Surface-coated Phosphors

著者 (5件)： Yan Wang (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology) ,  Li Wensheng (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology) ,  He Ling (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology) ,  An Guosheng (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology) ,  Hu Chunxia (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology)
資料名： Cailiao Daobao  (Cailiao Daobao)
巻： 30  号： 11B  ページ： 26-30,42  発行年： 2016年 
JST資料番号： C2126A  ISSN： 1005-023X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 熱安定性の良いSIO_2を層とし、ゾル-ゲル法を用いて、テトラエトキシシランをシリコン源とし、商用リン光粉体SRAL_2O_4を調製した。EU(2+),DY(3+)の表面を被覆し,高温での複合材料の調製における金属粒子の接触と高温酸化による消光の問題を解決した。ホットプレス焼結によって調製した複合材料の発光と摩擦特性に及ぼす被覆プロセスの影響を研究した。X線回折,走査型電子顕微鏡,および蛍光分光計を用いて,被覆の前後の光の表面モルフォロジーと発光特性を分析し,そして,複合材料の摩擦特性を,摩擦試験機によって研究した。結果は,光の表面被覆が,高温での酸化消光と接触消光を効果的に避けることができ,複合材料の摩耗抵抗を効果的に減少させ,複合材料の耐摩耗性を改善し,被覆率が10%のとき,複合材料のルミネセンス特性と耐摩耗性が最も良いことを示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： ホットプレス ,  ゾル-ゲル法 ,  耐摩耗性 ,  高温 ,  摩擦試験 ,  *被覆 ,  被覆率 ,  *表面被覆 ,  熱安定性 ,  消光 ,  走査電子顕微鏡 ,  *複合材料
準シソーラス用語： 表面形態 ,  *摩擦特性 , 【Automatic Indexing@JST】

著者キーワード (5件)： phosphorescent particle ,  encapsulation ,  quenching ,  composite material ,  friction and wear

分類 (3件)： セラミック・陶磁器の製造  (YC03020V) ,  金属材料へのセラミック被覆  (YC02050V) ,  防食  (WB03040M)

物質索引 (1件)： テトラエトキシシラン

タイトルに関連する用語 (5件)： Cu ,  複合材料 ,  摩擦特性 ,  表面被覆 ,  研究