Mo/Ti-3SiC_2積層複合材料の高温界面相安定性【Powered by NICT】

High temperature interfacial phase stability of a Mo/Ti₃SiC₂ laminated composite

著者 (5件)： Yi Yaoyong (Guangdong Welding Institute (China-Ukraine E. O. Paton Institute of Welding), Guangzhou 510650, PR China) ,  Ngai Tungwai (National Engineering Research Center of Near-Net-Shape Forming Technology for Metallic Materials, South China University of Technology, Guangzhou 510640, PR China) ,  Wang Andi (National Engineering Research Center of Near-Net-Shape Forming Technology for Metallic Materials, South China University of Technology, Guangzhou 510640, PR China) ,  Zhang Peng (College of Chemistry and Chemical Engineering, Yangtze Normal University, Chongqing 408100, PR China) ,  Li Liejun (National Engineering Research Center of Near-Net-Shape Forming Technology for Metallic Materials, South China University of Technology, Guangzhou 510640, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 9  ページ： 10951-10956  発行年： 2016年07月 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Mo/Ti_3SiC_2積層複合材は,50MPaの圧力下で1300°Cでスパークプラズマ焼結により調製した。Al粉末はTi_3SiC_2の生成を促進するための焼結助剤として用いた。作製した複合材料は,真空中で800°C,1000°Cおよび1150°Cでアニールした5 10 20および40hの高温での複合材料の界面相安定性を研究した。三つの界面層,すなわちMo_2C層,AlMoSi層とTi_5Si_3固溶体層は焼結時に形成された。実験結果は,本研究で調製したMo/Ti_3SiC_2層状複合材料は少なくとも1000°Cまで良好な界面相安定性を有し,界面層の成長はアニーリング時間に強い依存性を示さないことを示した。しかし,1150°Cに10h曝露した後,界面に形成された亀裂。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *複合材料 ,  粉末冶金 ,  *高温 ,  焼結 ,  *界面 ,  焼なまし ,  放電プラズマ焼結 ,  *相安定性 ,  亀裂 ,  アルミニウム ,  固溶体
準シソーラス用語： 界面層 ,  焼結助剤 ,  *積層 ,  *積層複合材料 , 【Automatic Indexing@JST】

著者キーワード (5件)： Mo/Ti3SiC2 ,  積層複合材料 ,  放電プラズマ焼結(SPS) ,  粉末冶金 ,  界面相安定性

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (5件)： Mo ,  Ti ,  積層複合材料 ,  界面 ,  相安定性