Evolution of mechanical properties and microstructure of a 3A21 Al alloy after fire exposure

著者 (6件)： Yang Pingxi (State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals,Lanzhou University of Technology) ,  Song Wenming (State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals,Lanzhou University of Technology) ,  Yang Guirong (State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals,Lanzhou University of Technology) ,  Li Jian (Wuhan Research Institute of Materials Protection) ,  Ma Ying (State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals,Lanzhou University of Technology) ,  Hao Yuan (State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals,Lanzhou University of Technology)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 37  号： 11  ページ： 30-39  発行年： 2016年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 3A21アルミニウム合金に対して,異なる熱曝露温度,保持時間および冷却速度の熱処理を行い,火災の発生過程をシミュレーションし,そして,機械的性質および微細構造を評価した。結果は以下を示す。冷却温度が510°C以下の場合,冷却方法は衝撃靭性に大きな影響を及ぼし,衝撃吸収エネルギーは204°Cで65%増加し,427°Cでは57%上昇した。火災温度が510°Cより低いとき,機械的性質は,火災温度の上昇とともにわずかに低下し,そして,火災の温度が657°Cに達したとき,機械的性質は29%~47%減少した。衝撃と引張破壊の両方においてディンプルのサイズが大きくなり、ディンプル内に粒状が現れ、火災の温度が上昇するにつれて、ミクロ組織は初期の微細な帯状組織の組織から次第に粗大化し、消失、再結晶、相相の析出、一部の溶解と結晶粒界の再析出になる。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 保持時間 ,  *アルミニウム合金 ,  冷却速度 ,  *機械的性質 ,  再結晶 ,  火災 ,  衝撃 ,  *微細構造 ,  結晶粒界
準シソーラス用語： ディンプル ,  引張破壊 ,  衝撃吸収 ,  衝撃靱性 ,  冷却温度 , 【Automatic Indexing@JST】