Effect of heating rate during primary crystallization on soft magnetic properties of melt-spun Fe-B alloys

著者 (8件)： Zang B. (Department of Materials Science and Engineering, Monash University, Clayton, VIC 3800, Australia) ,  Parsons R. (Department of Materials Science and Engineering, Monash University, Clayton, VIC 3800, Australia) ,  Onodera K. (Toyota Motor Corporation, Mishuku, Susono, Shizuoka 410-1193, Japan) ,  Kishimoto H. (Toyota Motor Corporation, Mishuku, Susono, Shizuoka 410-1193, Japan) ,  Kato A. (Toyota Motor Corporation, Mishuku, Susono, Shizuoka 410-1193, Japan) ,  Liu A.C.Y. (Monash Centre for Electron Microscopy, Monash University, Clayton, VIC 3800, Australia) ,  Liu A.C.Y. (School of Physics and Astronomy, Monash University, Clayton, VIC 3800, Australia) ,  Suzuki K. (Department of Materials Science and Engineering, Monash University, Clayton, VIC 3800, Australia)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 132  ページ： 68-72  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 150K/sまでの範囲の加熱速度(α)のアニールした非晶質Fe_87 B_13Cu_(0~1.5)の構造と磁気的性質を調べた。αは1.7から150K/sに増加したとき結晶化後Fe_87B_13の最低保磁力(H,C)はA/m174A/m6.7に劇的な減少を示した。150K/sでアニールしたFe_87 B_13Cuの保磁力はCu添加によって減少し,H_3.0A/mは=1.5で得られた。15~20nmの粒径を有するナノ構造はこれらの急速アニールした合金からの透過型電子顕微鏡写真で明らかであった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 焼なまし ,  非晶質 ,  粒径 ,  透過型電子顕微鏡 ,  磁気的性質 ,  ナノ構造 ,  *結晶化 ,  保磁力 ,  *溶融紡糸 ,  高速度 ,  *加熱速度 ,  銅 ,  *合金
準シソーラス用語： *軟磁性 , 【Automatic Indexing@JST】

著者キーワード (5件)： 核形成 ,  ガラス転移 ,  ランダム異方性 ,  Coercivity ,  粒径

分類 (1件)： 磁気的性質  (WB02020J)

タイトルに関連する用語 (6件)： 溶融紡糸 ,  Fe ,  B合金 ,  軟磁気特性 ,  結晶化 ,  加熱速度