ダイカストAZ91Dマグネシウム合金のミクロ組織と腐食挙動に及ぼす熱処理の影響を研究した。【JST・京大機械翻訳】

Effect Research of Heat Treatment on Microstructure and Corrosion Properties for Die-Casting AZ91DMg Alloy

著者 (6件)： Liu Baosheng (College of Materials Science and Engineering, Taiyuan University of Science and Technology) ,  Chai Yuesheng (College of Materials Science and Engineering, Taiyuan University of Science and Technology) ,  Zhang Mingang (College of Materials Science and Engineering, Taiyuan University of Science and Technology) ,  Fang Daqing (College of Materials Science and Engineering, Taiyuan University of Science and Technology) ,  Zhang Kewei (College of Materials Science and Engineering, Taiyuan University of Science and Technology) ,  Wei Yinghui (College of Materials Science and Engineering,Taiyuan University of Technology)
資料名： Taiyuan Ligong Daxue Xuebao  (Taiyuan Ligong Daxue Xuebao)
巻： 47  号： 4  ページ： 460-465  発行年： 2016年 
JST資料番号： C2209A  ISSN： 1007-9432  CODEN： TLDXF3  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ダイカスト,溶体化(T4)および人工時効(T6)のAZ91Dマグネシウム合金の微細構造進展および腐食挙動を,金属顕微鏡,XRD,SEM,分極曲線および塩水噴霧腐食試験によって研究した。結果は,Β-MG_(17)AL_(12)相が,415°Cで6時間の熱処理の後に,AZ91Dマグネシウム合金で完全に溶解することを示した。200°Cで2時間時効した後,Β相は最初に結晶粒界に析出し,時効時間の増加とともに析出相は徐々に増加した。T4サンプルはΒ相の溶解により、その耐腐食性が最も良く、局部に微小腐食点が形成され、T6サンプルはボタン腐食効果により、耐腐食性が最も悪く、しかも時効時間が延長するにつれて、耐腐食性が次第に低下する。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 結晶粒界 ,  腐食試験 ,  耐食性 ,  金属顕微鏡 ,  溶体化処理 ,  *腐食 ,  X線回折 ,  *ダイカスト ,  時効
準シソーラス用語： 水噴霧 ,  分極曲線 ,  微細構造進展 ,  人工時効 ,  *腐食挙動 ,  *AZ91D , 【Automatic Indexing@JST】

著者キーワード (5件)： die-casting AZ91DMg alloy ,  solid solution treatment ,  artificial aging ,  microstructure ,  corrosion resistance

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  腐食  (WB03030B)

タイトルに関連する用語 (6件)： ダイカスト ,  AZ91Dマグネシウム合金 ,  ミクロ組織 ,  腐食挙動 ,  熱処理 ,  研究