2.5D SiC_f/SiO_2複合材料の強度改善に関するZrO_2被覆の効果【Powered by NICT】

Effects of ZrO₂ coating on the strength improvement of 2.5D SiC_f/SiO₂ composites

著者 (4件)： Wang Qing (Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073, Hunan, PR China) ,  Cao Feng (Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073, Hunan, PR China) ,  Xiang Yang (Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073, Hunan, PR China) ,  Peng Zhi-hang (Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073, Hunan, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 1 PA  ページ： 884-889  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,二酸化ジルコニウム(ZrO_2)被覆を持つ2.5次元KD II炭化けい素繊維強化二酸化けい素(2.5D(SiC_f/SiO_2))セラミックマトリックス複合材料をゾル-ゲル法で作製することに成功した。複合材料の曲げ強度に及ぼすZrO_2被覆の影響を包括的に調べた。結果はZrO_2~-被覆SiC_f/SiO_2複合材料の曲げ強さは被覆無しの複合材料のそれの約2倍であることを示した。さらに,1200°Cで試験した複合材料の強度は室温で試験した試料のそれよりも約12%増加した。さらに,複合材料の酸化挙動を1300及び1500°Cに対応する高温,SiC繊維とSiO_2マトリックス間の結合強度の増加を示したで調べた。ミクロ組織の進展はZrO_2被覆は繊維とマトリックス間の効果的な結合のために繊維の表面粗さの増加をもたらしたことを明らかにした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 二酸化ケイ素 ,  酸化ジルコニウム ,  高温 ,  炭化ケイ素 ,  ゾル-ゲル法 ,  *複合材料 ,  付着強さ ,  繊維強化 ,  曲げ強さ ,  *被覆
準シソーラス用語： 酸化挙動 ,  2.5次元 , 【Automatic Indexing@JST】

著者キーワード (4件)： セラミック複合材料 ,  被覆 ,  機械的性質 ,  高温

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (1件)： 複合材料