高密度スルホアルミネートセメントコンクリートの性質に及ぼす被覆した凝集体に及ぼすペースト厚さの影響【Powered by NICT】

Influence of paste thickness on coated aggregates on properties of high-density sulphoaluminate cement concrete

著者 (5件)： Sun Keke (Shandong Provincial Key Laboratory of Preparation and Measurement of Building Materials, Jinan, Shandong 250022, China) ,  Zhou Xiangming (Department of Mechanical, Aerospace and Civil Engineering, Brunel University London, Uxbridge, Middlesex UB8 3PH, United Kingdom) ,  Gong Chenchen (Shandong Provincial Key Laboratory of Preparation and Measurement of Building Materials, Jinan, Shandong 250022, China) ,  Ding Yanyu (Shandong Provincial Key Laboratory of Preparation and Measurement of Building Materials, Jinan, Shandong 250022, China) ,  Lu Lingchao (Shandong Provincial Key Laboratory of Preparation and Measurement of Building Materials, Jinan, Shandong 250022, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 115  ページ： 125-131  発行年： 2016年07月15日 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ち密化調合設計アルゴリズムとFuller曲線のための改良された方法は,高密度スルホアルミネートセメントコンクリート(HDSC)を設計した。HDSCの性能は,被覆凝集体に及ぼすペースト厚さに大きく影響される。3種類のペースト厚さt=10μm,20μm,30μm,水結合材比0.25,0.30及び0.35で被覆した骨材を含むスルホアルミン酸セメントコンクリート混合物を調製した。実験の結果は,被覆凝集体に及ぼすペースト厚さはHDSCの機械的性質と耐久性に著しく影響することを示した。ペースト厚さの増加と共に,圧縮強さは増加するが,電気抵抗率は減少し,特に1と3日の若材齢であった。HDSCの硫酸塩腐食抵抗係数は1.0より大きく,全気孔率は7%未満であることができ,ミクロ細孔(細孔径20nm以下)は70%より大きくなる可能性がある。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *凝集体 ,  *被覆 ,  空隙率 ,  耐久性 ,  *ペースト ,  硫酸塩 ,  細孔 ,  圧縮強さ ,  緻密化 ,  *セメントコンクリート ,  細孔径 ,  電気抵抗率
準シソーラス用語： 若材令 ,  水結合材比 ,  *高密度 , 【Automatic Indexing@JST】

著者キーワード (5件)： スルホアルミン酸セメントコンクリート ,  Fuller曲線 ,  高密度混合物設計アルゴリズム ,  被覆厚さ ,  耐久性