PECHINIゾル-ゲル法に基づく色素増感太陽電池の最適化【JST・京大機械翻訳】

Optimization of Dye-sensitized Solar Cells Prepared by Pechini Sol-Gel Method

著者 (6件)： Yin Yuefeng (Hubei Key Laboratory of Low Dimensional Optoelectronic Materials and Devices, Hubei University of Arts and Science) ,  Liang Guijie (Hubei Key Laboratory of Low Dimensional Optoelectronic Materials and Devices, Hubei University of Arts and Science) ,  Zhang Qiang (Hubei Key Laboratory of Low Dimensional Optoelectronic Materials and Devices, Hubei University of Arts and Science) ,  Pan Zheng (Hubei Key Laboratory of Low Dimensional Optoelectronic Materials and Devices, Hubei University of Arts and Science) ,  Li Wangnan (Hubei Key Laboratory of Low Dimensional Optoelectronic Materials and Devices, Hubei University of Arts and Science) ,  Li Zaifang (Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 31  号： 7  ページ： 739-744  発行年： 2016年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 機能性TIO_2薄膜を,ゾル-ゲル法によって調製し,界面電荷複合効果に基づいて,TIO_2膜の厚さが電池の光電特性に及ぼす影響を研究し,膜厚の制御により電池性能を最適化した。UV-VIS,電気化学インピーダンススペクトル,およびI-V試験を用いて,TIO_2膜厚が染料の吸着量,界面電子の複合プロセス,および電池の光電特性に及ぼす影響を研究した。結果は,TIO_2膜厚が増加するにつれて,染料の吸着容量が増加し,光電流効率が増加することを示した。同時に,TIO_2膜中の電子寿命は短くなり,TIO_2/電解質界面の電子複合確率が増大すると,光電子圧力が低下した。これらの総合的効果により,電池効率は最初に増加し,次に減少し,そして,膜厚が10.7ΜMのとき,光電変換効率は,最適値(7.75%)に達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *電池 ,  電気化学 ,  界面 ,  *最適化 ,  インピーダンススペクトル ,  電荷 ,  光電流 ,  膜厚 ,  *ゾル-ゲル法
準シソーラス用語： 光電変換効率 ,  吸着容量 ,  吸着量 ,  電池性能 ,  光電気 ,  *色素増感太陽電池 , 【Automatic Indexing@JST】

著者キーワード (4件)： dye-sensitized solar cells ,  pechini Sol-Gel method ,  TiO_2 film thickness ,  interfacial charge recombination

分類 (1件)： 太陽電池  (NC03084O)

タイトルに関連する用語 (4件)： ゾル ,  ゲル ,  色素増感太陽電池 ,  最適化