加熱速度は22MNB5超高強度鋼奥氏体化の影響【JST・京大機械翻訳】

Effect of Heating Rate on Austenitization of 22MnB5Ultra High Strength Steel

著者 (5件)： Jin Yongming (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology) ,  Zhang Yisheng (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology) ,  Liang Weikang (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology) ,  Zheng Xuyu (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology) ,  Li Yang (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology)
資料名： Jixie Gongcheng Cailiao  (Jixie Gongcheng Cailiao)
巻： 40  号： 4  ページ： 80-83  発行年： 2016年 
JST資料番号： C2051A  ISSN： 1000-3738  CODEN： JGCAEL  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： GLEEBLE3500型熱シミュレーション試験機上の22MNB5超高強度鋼に対して,異なる加熱速度(10~100°CS(-1))の下でオーステナイト化を行い,加熱速度がオーステナイト化温度A_(C1)が検討した,A_(C3)およびオーステナイト転移時間の影響,そしてとA_(C1)の加熱速度の関係式を確立した。結果:この鋼のA_(C1)とA_(C3)は,いずれも加熱速度の増大につれてに増加した;加熱速度が25°CS(-1)より低いとき,加熱速度の増大につれて急速に増加しA_(C1),25°CS(-1)より高かったとき,A_(C1)緩やかに一定傾向増加を示した;オーステナイト,オーステナイト化温度区間(A_(C3)-A_(C1))の大きさには上昇の傾向を呈し,加熱速度の向上に伴い時間短縮が転移した。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 高速度 ,  オーステナイト ,  試験装置 ,  *鋼 ,  *加熱速度
準シソーラス用語： 時間短縮 ,  オーステナイト化 ,  熱シミュレーション ,  *超高強度鋼 , 【Automatic Indexing@JST】

著者キーワード (4件)： 22MnB5 ultra high strength steel ,  thermo-mechanical simulation ,  heating rate ,  austenitization