Y₂O₃-ZnOドープ(Zr_0.8Sn_0.2)TiO₄セラミックスの焼結挙動とマイクロ波誘電特性

Sintering behavior and microwave dielectric properties of Y2O3-ZnO doped (Zr0.8Sn0.2)TiO4 ceramics

著者 (6件)： Sun Qinglei (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, China) ,  Zhou Hongqing (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, China) ,  Zhu Haikui (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, China) ,  Qi Hongqing (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, China) ,  Hu Lisong (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, China) ,  Yue Zhenxing (State Key Laboratory of New Ceramics and Fine Processing, Tsinghua University, Beijing, China)
資料名： Journal of Materials Science. Materials in Electronics  (Journal of Materials Science. Materials in Electronics)
巻： 27  号： 8  ページ： 7750-7754  発行年： 2016年08月 
JST資料番号： W0003A  ISSN： 0957-4522  CODEN： JMTSAS  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 従来の固相反応法によって,(Zr_0.8Sn_0.2)TiO₄(ZST)セラミックスを作製した。Y₂O₃-ZnOドープZSTセラミックスの焼結挙動,相組成,微細構造及びマイクロ波誘電特性を調べた。単一ZST相のみがX線回折パターンによって同定された。誘電率並びにQ×f値の変動傾向は,バルク密度に従った。適切なY₂O₃及びZnOを添加することによって,焼結温度が1240°Cまで効果的に減少するだけでなく,ZSTセラミックの緻密性及びマイクロ波誘電特性が顕著に改善された。しかし,過度の添加は,試料の微細構造及び全体特性を悪化させた。1240°Cで焼結した0.5重量%Y₂O₃を添加した1重量%ZnOドープZSTセラミックスにおいて,39.73の誘電率ε_r,48,545GHz(5.5GHzにおいて)のQ×f値及び-2.13ppm/°Cのτ_f値が得られた。Copyright 2016 Springer Science+Business Media New York Translated from English into Japanese by JST.