ナノ複合材料の特性に及ぼすナノTIO_2含有量の影響を研究した。【JST・京大機械翻訳】

Effects of Nano TiO_2 Content on Properties of PVC/Rice Husk Powder Wood-Plastic Composites

著者 (5件)： Wang Xuanbo (College of Engineering,Nanjing Agricultural University,Jiangsu Key Laboratory for Intelligent Agricultural Equipment) ,  Chen Xiaodan (College of Engineering,Nanjing Agricultural University,Jiangsu Key Laboratory for Intelligent Agricultural Equipment) ,  Chen Jiawei (College of Engineering,Nanjing Agricultural University,Jiangsu Key Laboratory for Intelligent Agricultural Equipment) ,  Liu Yutao (College of Engineering,Nanjing Agricultural University,Jiangsu Key Laboratory for Intelligent Agricultural Equipment) ,  Yao Xuexia (College of Engineering,Nanjing Agricultural University,Jiangsu Key Laboratory for Intelligent Agricultural Equipment)
資料名： Gongcheng Suliao Yingyong  (Gongcheng Suliao Yingyong)
巻： 44  号： 7  ページ： 31-36  発行年： 2016年 
JST資料番号： C2099A  ISSN： 1001-3539  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： PVC/籾殻複合材料を,ナノTIO_2,籾殻粉,ポリ塩化ビニル(PVC),および安定化剤の混合によって,押出成形によって調製した。PVC/籾殻複合材料の性質に及ぼすナノTIO_2添加量の影響を研究した。実験結果は,ナノ複合材料の機械的性質,耐水性および熱安定性が,ナノTIO_2含有量の増加とともに,最初に増加し,次に減少したが,複合材料の表面色は,ナノTIO_2含有量の増加とともに,徐々に薄くなった。ナノTIO_2含有量が1.00PHRのとき,複合材料の引張強さ,衝撃強さおよび曲げ強さは,それぞれ,40.6%,62.2%および19.7%増加した。8Dの吸水率は2.5%から1.6%に低下し,表面接触角は78.5°から82.1°に増加し,800°Cでのチャー収率は21.1%から29.5%に増加した。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 衝撃強さ ,  安定剤 ,  熱安定性 ,  *ナノ複合材料 ,  吸水率 ,  押出成形 ,  *複合材料 ,  接触角 ,  機械的性質 ,  引張強さ ,  粉体 ,  チャー ,  耐水性
準シソーラス用語： 表面色 , 【Automatic Indexing@JST】

著者キーワード (6件)： nano TiO_2 ,  rice husk ,  poly(vinyl chloride) ,  mechanical property ,  water absorption property ,  thermal property