Ho³⁺をドープしたゲルマニウム酸テルルガラスの2~3μm発光と蛍光減衰挙動

2-3μm emission and fluorescent decaying behavior in Ho³⁺-doped tellurium germanate glass

著者 (8件)： Gao Song (Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China) ,  Gao Song (University of Chinese Academy of Sciences, Beijing 100049, China) ,  Liu Xueqiang (Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China) ,  Liu Xueqiang (University of Chinese Academy of Sciences, Beijing 100049, China) ,  Kang Shuai (Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China) ,  Kang Shuai (University of Chinese Academy of Sciences, Beijing 100049, China) ,  Liao Meisong (Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China) ,  Hu Lili (Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China)
資料名： Optical Materials  (Optical Materials)
巻： 53  ページ： 44-47  発行年： 2016年03月 
JST資料番号： W0468A  ISSN： 0925-3467  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,Ho₂O₃をドープした33GeO₂-30TeO₂-27PbO-10CaO(モル%)ガラスの640nmレーザ励起のもとでの2.05μm発光と約3μmでの広いバンドスペクトルについて報告した。Ho³⁺での⁵I₇→⁵I₈と⁵I₆→⁵I₇遷移に起因した明確なスペクトルを観測した。2.05μmの発光強度と約3μmの広いバンドのFWHMでの全幅はHo濃度に依存した。Ho³⁺のピーク誘導放出断面積は,McCumber理論で計算すると,2.05μmで6.57×10^-21cm²であった。2700nmから3050nmまでの広い平らな発光帯を2モル%のHo₂O₃をドープしたゲルマン酸テルルガラスにおいて観測した。⁵I₇状態の寿命はHo³⁺濃度の増加とともに,非放射緩和過程のために減少した。エネルギー移動係数として271.88mol^-1s^-1を得た。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： ガラス ,  *蛍光減衰 ,  エネルギー移動 ,  ホルミウム ,  ドーピング ,  パラメータ ,  発光スペクトル ,  電子遷移 ,  テルル化合物
準シソーラス用語： *ゲルマニウム酸塩ガラス ,  Judd-Ofeltパラメータ

著者キーワード (5件)： Tellurium germanate glass ,  Ho³⁺ ,  2.05μm ,  ~3μm ,  Fluorescent decaying