固相再生MG-ND-ZN-ZRマグネシウム合金の時効強化【JST・京大機械翻訳】

Aging strengthening of Mg-Nd-Zn-Zr magnesium alloy prepared by solid recycling process

著者 (7件)： Wen Lihua (School of Mechanical and Electrical Engineering, Heilongjiang Institute of Technology) ,  Ji Zesheng (School of Materials Science and Engineering, Harbin University of Science and Technology) ,  Xu Hongyu (School of Materials Science and Engineering, Harbin University of Science and Technology) ,  Wang Baoqin (School of Mechanical and Electrical Engineering, Heilongjiang Institute of Technology) ,  Ning Huiyan (School of Mechanical and Electrical Engineering, Heilongjiang Institute of Technology) ,  Weng Jiangxiang (School of Mechanical and Electrical Engineering, Heilongjiang Institute of Technology) ,  Hu Maoliang (School of Materials Science and Engineering, Harbin University of Science and Technology)
資料名： Zhongguo Youse Jinshu Xuebao  (Zhongguo Youse Jinshu Xuebao)
巻： 26  号： 7  ページ： 1408-1413  発行年： 2016年 
JST資料番号： W0943A  ISSN： 1004-0609  CODEN： ZYJXFK  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 固相再生MG-2.4ND-0.4ZN-0.4ZRマグネシウム合金の等温時効過程の析出強化挙動を研究した。時効析出物のモルフォロジーと破壊挙動をTEMとSEMによって分析した。結果は以下を示す。合金の機械的性質は,200°C,16時間時効処理後にピークに達し,引張強さは294.5MPA,伸びは13.5%であった。その際、結晶粒が分散し、ロッド状Β相安定相と板状Β相安定相が析出し、合金の高い強度が得られた。200°C,60Hの過時効処理の下で,Β相は,Β相安定相に成長し,そして,合金の強度は減少し,そして,塑性は増加した。時効処理の間,合金は粒内せん断破壊を主とし,ピーク時効の際に合金は粒界破壊と粒界破壊を主とし,過時効の際の粗大二次破壊過程には大きな影響がある。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 結晶粒 ,  析出物 ,  粒界破壊 ,  *時効 ,  モルフォロジー ,  過時効 ,  引張強さ ,  塑性 ,  *固相 ,  伸び ,  析出硬化 ,  剪断破壊 ,  *合金 ,  *マグネシウム合金
準シソーラス用語： 過時効処理 , 【Automatic Indexing@JST】

著者キーワード (5件)： Mg-Nd-Zn-Zr magnesium alloy ,  aging strengthening ,  microstructure ,  mechanical property ,  fracture behavior

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： 固相 ,  マグネシウム合金 ,  時効 ,  強化