W濃度の関数としての650°Cにおける二元Ti-xW(0≦x≦30,wt%)合金の酸化挙動

Oxidation behavior of binary Ti-xW (0≦x≦30, wt%) alloys at 650°C as a function of W concentration

著者 (4件)： Samimi P. (Department of Materials Science and Engineering, Iowa State University, Ames, Iowa, 50011, United States) ,  Samimi P. (The Center for Advanced Non-Ferrous Structural Alloys (CANFSA), a joint NSF I/UCRC between the Colorado School of Mines (Golden, CO 80401) and the Iowa State University (Ames, IA 50011), United States) ,  Collins P.C. (Department of Materials Science and Engineering, Iowa State University, Ames, Iowa, 50011, United States) ,  Collins P.C. (The Center for Advanced Non-Ferrous Structural Alloys (CANFSA), a joint NSF I/UCRC between the Colorado School of Mines (Golden, CO 80401) and the Iowa State University (Ames, IA 50011), United States)
資料名： Corrosion Science  (Corrosion Science)
巻： 111  ページ： 531-540  発行年： 2016年10月 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 650°CでのTi-W系の酸化挙動に対する組成の役割を,組成傾斜した試料Ti-xW(0≦x≦30,全ての組成はwt%)を用いて調査した。ベース材のミクロ構造の変化と酸化物層の厚さを組成の関数として評価した。αラス,βリブ/析出物,ラメラ構造を含むベース材のミクロ構造に関する観察のいくつかは,Ti-Mo系について報告されたものに共通することが判明した。より薄い酸化物の形成は必ずしも低酸素侵入を意味するとは限らないことを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 二元合金 ,  *チタン合金 ,  タングステン添加合金 ,  合金元素 ,  傾斜機能材料 ,  化学組成 ,  *酸化膜 ,  厚み ,  α相 ,  β相 ,  析出物 ,  ラメラ ,  酸素 ,  濃度依存性 ,  加熱温度 ,  *高温酸化 ,  スケール
準シソーラス用語： 組成傾斜