UV硬化水性超分岐ポリエステルの調製研究【JST・京大機械翻訳】

Development of UV curing waterborne hyperbranched polyester

著者 (8件)： Yang Baoping (Institute of Petrochemical Technology,Lanzhou University of Technology) ,  Chang Jie (Institute of Petrochemical Technology,Lanzhou University of Technology) ,  Guo Junhong (Institute of Petrochemical Technology,Lanzhou University of Technology) ,  Bao Xuemei (Institute of Petrochemical Technology,Lanzhou University of Technology) ,  Li Minrui (Institute of Petrochemical Technology,Lanzhou University of Technology) ,  Mu Bo (Institute of Petrochemical Technology,Lanzhou University of Technology) ,  Zhao Qiuping (Institute of Petrochemical Technology,Lanzhou University of Technology) ,  Cui Jinfeng (Institute of Petrochemical Technology,Lanzhou University of Technology)
資料名： Huagong Xinxing Cailiao  (Huagong Xinxing Cailiao)
巻： 44  号： 4  ページ： 60-62  発行年： 2016年 
JST資料番号： C2923A  ISSN： 1006-3536  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ペンタエリスリトールを核、2であった,第1世代の超分岐ポリエステルを,2-ジメチロールプロピオン酸腕を単量体として合成した;次に第1世代の超分岐ポリエステルを核として,2,2-ジメチロールプロピオン酸腕を単量体として,アクリル酸クロリドとマレイン酸無水物を用いて第2世代超分岐ポリエステル改質を行った。第2世代の超分岐ポリエステルを合成し,UV硬化性水性超分岐ポリエステルを合成し,その赤外スペクトルと示差熱分析,を行った。、塗膜性能に及ぼすマレイン酸無水物用量,アクリル酸塩化物の影響を研究した。結果は超分岐ポリエステルとアクリル酸クロリドとマレイン酸無水物三者の物質のモル比が1:6:8であるとき,水性超分岐ポリエステルの安定性と塗膜の耐水性が比較的に良いことを示した。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 示差熱分析 ,  モル比 ,  *塗膜 ,  耐水性 ,  赤外スペクトル ,  塩化物 ,  単量体 ,  脂肪族カルボン酸 ,  ビニル化合物 ,  不飽和カルボン酸 ,  脂肪族アルコール
準シソーラス用語： マレイン酸無水物 ,  *紫外線硬化 , 【Automatic Indexing@JST】

著者キーワード (3件)： UV curing ,  waterborne ,  hyperbranched polyester

分類 (1件)： 共重合  (CG04030D)

物質索引 (3件)： アクリル酸 ,  アクリル酸クロリド ,  ペンタエリスリトール

タイトルに関連する用語 (5件)： UV硬化 ,  分岐 ,  ポリエステル ,  調製 ,  研究