Q235鋼,3Y-TZP/LZAS微結晶ガラスの勾配コーティングエロージョン摩耗性能を研究した。【JST・京大機械翻訳】

Research on Erosion Wear Resistance of 3Y-TZP/LZAS Glass-ceramic Gradient Coatings on Q235 Steel Substrate

著者 (6件)： Liu Jianhao (School of Manufacturing Science and Engineering, Southwest University of Science and Technology) ,  Gong Wei (School of Manufacturing Science and Engineering, Southwest University of Science and Technology) ,  Zhong Liang (School of Manufacturing Science and Engineering, Southwest University of Science and Technology) ,  Han Teng (School of Manufacturing Science and Engineering, Southwest University of Science and Technology) ,  Zhang Wenli (School of Manufacturing Science and Engineering, Southwest University of Science and Technology) ,  Liu Kaixiang (School of Materials Science and Engineering, Southwest University of Science and Technology)
資料名： Zhongguo Taoci  (Zhongguo Taoci)
巻： 52  号： 3  ページ： 59-64  発行年： 2016年 
JST資料番号： C2267A  ISSN： 1001-9642  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 鋼Q235を調製した。焼結塗Tang法を用いて3Y-TZP/LZASガラスセラミック勾配コーティング。自作のエロージョン磨耗,15°、30°45°60°と75°と90°の衝突角度では,エロージョン腐食時間を制御する試験機を用いて,それぞれ異なる層勾配コーティングに対してエロージョンを行い,体積をジョン摩耗速度を測定した。SEMによりエロージョン腐食後の試料表面の微細構造分析を行い,異なるエロージョン角度下での勾配被覆のエロージョン摩耗機構を研究した。結果:傾斜被覆の体積摩耗速度はジョンエロージョン角度とともに増大して,いずれも先に増大した後減少する傾向を示した,そして60。のとき最大値に達した;勾配コーティングのエロージョン摩耗性能は,層数の増加に伴い強まった;低角度でのエロージョンメカニズムは主に摩耗切削、掘り起こし効果による切削のために,高角度でのエロージョン機構は主に捶撃鍛効果を引き起こすたたく脆性破断であるが,60°の衝突角度で捶撃効果と切削鍛造、掘り起こし効果がいずれも強く,摩耗量は最大コーティング。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 破断 ,  ガラスセラミック ,  *微結晶 ,  エロージョン腐食 ,  鋼 ,  切削 ,  *摩耗 ,  脆性 ,  *被覆 ,  摩耗速度
準シソーラス用語： 摩耗量 ,  衝突角度 ,  *エロージョン ,  *Q235 ,  *エロージョン摩耗 , 【Automatic Indexing@JST】

著者キーワード (4件)： Glass-ceramic ,  Gradient coating ,  Erosion angle ,  Erosion mechanism

分類 (2件)： 機械的性質  (WB02030U) ,  腐食  (WB03030B)

タイトルに関連する用語 (7件)： Q235鋼 ,  微結晶 ,  ガラス ,  勾配 ,  コーティング ,  エロージョン摩耗 ,  研究