-合金3YC61の強靭化プロセス【JST・京大機械翻訳】

Strengthening heat treatment process of iron-nickel based 3YC61 alloy

著者 (5件)： Huang Guoping (Chongqing Materials Research Institute Co.,Ltd., National Engineering Research Center for Instrument Functional Materials, Chongqing Key Laboratory of Corrosion Resistance Alloys) ,  Tang Rui (Chongqing Materials Research Institute Co.,Ltd., National Engineering Research Center for Instrument Functional Materials) ,  Liu Haiding (Chongqing Materials Research Institute Co.,Ltd., National Engineering Research Center for Instrument Functional Materials, Chongqing Key Laboratory of Corrosion Resistance Alloys) ,  Wang Dongzhe (Chongqing Materials Research Institute Co.,Ltd., National Engineering Research Center for Instrument Functional Materials, Chongqing Key Laboratory of Corrosion Resistance Alloys) ,  Li Yongyou (Chongqing Materials Research Institute Co.,Ltd., National Engineering Research Center for Instrument Functional Materials, Chongqing Key Laboratory of Corrosion Resistance Alloys)
資料名： Jinshu Rechuli  (Jinshu Rechuli)
巻： 41  号： 6  ページ： 151-154  発行年： 2016年 
JST資料番号： C2061A  ISSN： 0254-6051  CODEN： JRECDB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 高の石油探査、採掘に使用される設備は、媒体、温度、圧力の影響を受け、応力腐食と応力腐食破壊(SSCとSCC)が起こりやすく、これは金属材料の力学と耐腐食性に対して厳しい要求を提出した。本論文では、-合金3YC61の強靱化技術について系統的な研究を行った。3YC61合金の最適熱処理温度は980~1000°Cであった。最適時効処理温度は730~770°C,620~620°C+620°C×7H+AQの二段階時効処理(全時効時間18H)であった。合金の機械的性質はINCOLOY 925合金の性能指数に達した。直接時効処理により、3YC61合金の強度、靭性と塑性を同時に向上させ、合金の総合性能、特に強度は718718合金に近い。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 靱性 ,  応力腐食 ,  時効 ,  石油 ,  塑性 ,  金属材料 ,  機械的性質 ,  採掘 ,  耐食性 ,  *合金 ,  性能指数 ,  媒質
準シソーラス用語： 熱処理温度 ,  *強靱化 , 【Automatic Indexing@JST】