立方窒化ホウ素表面における窒化ホウ素の成長とメカニズムに関する研究【JST・京大機械翻訳】

Growth and Mechanism of the Spines on the Surface of cBN Abrasives

著者 (6件)： Gui Yanghai (Henan Collaborative Innovation Center of Environmental Pollution Control and Ecological Restoration,Zhengzhou University of Light Industry) ,  Wang Haiyan (Department of Material and Chemical Engineering,Zhengzhou University of Light Industry) ,  Ma Tiantian (Department of Material and Chemical Engineering,Zhengzhou University of Light Industry) ,  Wu Yiqian (Department of Material and Chemical Engineering,Zhengzhou University of Light Industry) ,  Li Kaili (Department of Material and Chemical Engineering,Zhengzhou University of Light Industry) ,  Li Dongwei (Department of Material and Chemical Engineering,Zhengzhou University of Light Industry)
資料名： Rengong Jingti Xuebao  (Rengong Jingti Xuebao)
巻： 45  号： 3  ページ： 799-802  発行年： 2016年 
JST資料番号： W0398A  ISSN： 1000-985X  CODEN： RJXUEN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 複合法を用いて、100/120粒径の立方晶窒化ホウ素(CBN)を母材とし、めっき浴に工業用不活性粉末炭化物Mを添加し、電気めっきメッキを行い、めっき後の製品をSEMとTG-DTAにより特性評価した。結果によると、複合後、CBNは角と凸凹面長がNie刺を持つだけでなく、元の平面めっき層上に長いノジュールがあり、粗さは大きく増加し、めっき後のCBNは464°C以下で原生料よりも良好な熱安定性があり、樹脂基磨具ではより良い使用温度がある。複合めっきのNI-MプロセスにおけるM添加量がめっき層の形態に与える影響を研究し、状生成物の成長メカニズムを検討した。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 熱安定性 ,  炭化物 ,  キャラクタリゼーション ,  電気めっき ,  めっき皮膜 ,  めっき液 ,  複合めっき ,  めっき ,  *窒化ホウ素 ,  団塊 ,  粉体 ,  粒径
準シソーラス用語： 使用温度 ,  TG-DTA ,  CBN【セラミック】 , 【Automatic Indexing@JST】

著者キーワード (4件)： cBN ,  copmposite electroplating ,  Ni spine ,  mechanism

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： 窒化ホウ素 ,  成長 ,  メカニズム ,  研究