Cu(45)Zr(45)Ag(10)金属ガラスにおける相分離と結晶化の直接TEM観察【Powered by NICT】

Direct TEM Observation of Phase Separation and Crystallization in Cu_(45)Zr_(45)Ag_(10) Metallic Glass

著者 (8件)： Wang Hui (School of Materials Science and Engineering, Beihang University) ,  Xiao Shanggang (School of Materials Science and Engineering, Beihang University) ,  Zhang Tao (School of Materials Science and Engineering, Beihang University) ,  Xu Qiang (Delft University of Technology, Kavli Institute of Nanoscience) ,  Liu Zengqian (Institute of Metal Research, Chinese Academy of Sciences) ,  Wu Mengyue (Delft University of Technology, Kavli Institute of Nanoscience) ,  Tichelaar Frans (Delft University of Technology, Kavli Institute of Nanoscience) ,  Zandbergen Henny (Delft University of Technology, Kavli Institute of Nanoscience)
資料名： Acta Metallurgica Sinica  (Acta Metallurgica Sinica)
巻： 29  号： 6  ページ： 538-545  発行年： 2016年 
JST資料番号： C5023A  ISSN： 1006-7191  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： Cu_(45)Zr(45)Ag(10)金属ガラスの構造変化をその場透過型電子顕微鏡加熱実験により調べた。相分離と結晶化の間の関係を明らかにした。初期段階での核形成と成長制御ナノスケール相分離はナノ結晶化を妨げることが分かったが,Agナノ粒子の凝集による粗い相分離がCuリッチナノ結晶の析出を促進することが分かった。組成と動力学不均一性の結合は,相分離前結晶化時に重要な役割を果たすと考えられた。Data from the ScienceChina, LCAS.【Powered by NICT】

シソーラス用語： ナノ結晶 ,  *相分離 ,  不均一性 ,  透過型電子顕微鏡 ,  *結晶化 ,  核形成 ,  成長調節 ,  *金属ガラス
準シソーラス用語： 銀ナノ粒子 ,  ナノ結晶化 ,  ナノスケール ,  構造変化 ,  *透過型電子顕微鏡法 , 【Automatic Indexing@JST】

著者キーワード (5件)： バルク金属ガラス ,  相分離 ,  その場TEM加熱 ,  結晶化 ,  ガラス形成能

分類 (1件)： 金属の結晶成長  (BK13030M)

タイトルに関連する用語 (7件)： Cu ,  Zr ,  Ag ,  金属ガラス ,  相分離 ,  結晶化 ,  TEM観察