700MPA級の自動車鋼の静的軟化挙動に及ぼすTIの影響を研究した。【JST・京大機械翻訳】

Effect of Ti on static recrystallization softening behavior of automobile beam steel with yield strength of 700 MPa

著者 (7件)： Li Yongliang (School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing) ,  Wang Fuming (School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing) ,  Li Changrong (School of Materials Science and Engineering,University of Science and Technology Beijing) ,  Yang Zhanbing (School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing) ,  Cao Ruifang (Shougang Corporation Qian’an Iron & Steel Co Ltd) ,  Zheng Yaxu (School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing) ,  He Yutian (School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 37  号： 10  ページ： 138-145  発行年： 2016年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 700MPA級の高強度自動車用鋼の静的軟化挙動に及ぼすTIの影響をGLEEBLE-3500熱シミュレーション試験機を用いて研究した。異なる温度と異なるパス間隔での「応力-歪曲」曲線を測定することによって,同じ条件の下でTIとTI含有鋼の再結晶体積分率を計算した。その結果,TIの添加は高温下で等軸結晶粒の成長を阻害するだけでなく,変形オーステナイトの静的再結晶挙動を抑制し,静的軟化率を低下させることが分かった。0.04%のTIを添加すると,静的再結晶活性化エネルギーは260KJ・MOL(-1)から321KJ・MOL(-1)に増加した。静的再結晶活性化エネルギーの増加はTI含有鋼中に形成された(TI,NB)(C,N)などの析出相が高温度で結晶粒界移動を阻害することに起因する。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： オーステナイト ,  試験装置 ,  体積率 ,  *自動車用鋼 ,  高温 ,  活性化エネルギー ,  *鋼 ,  結晶粒 ,  粒界移動 ,  再結晶
準シソーラス用語： 静的再結晶 ,  熱シミュレーション ,  高強度 ,  *軟化挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： automobile beam steel ,  static recrystallization ,  activation energy ,  precipitate