三段階時効7N01アルミニウム合金の微細構造と機械的性質の関係に関する研究【JST・京大機械翻訳】

The microstructure of a three-step-aged 7N01 aluminum alloy in relation with its mechanical properties

著者 (6件)： Rao Dong (Center for High Resolution Electron Microscopy, College of Material Science and Engineering, Hunan University) ,  Chen Jianghua (Center for High Resolution Electron Microscopy, College of Material Science and Engineering, Hunan University) ,  Yang Xiubo (Department of Applied Physics, School of Physics and Electronics, Hunan University) ,  Zhao Tiantian (Center for High Resolution Electron Microscopy, College of Material Science and Engineering, Hunan University) ,  Yu Xiongwei (Center for High Resolution Electron Microscopy, College of Material Science and Engineering, Hunan University) ,  Zhao Xinqi (Center for High Resolution Electron Microscopy, College of Material Science and Engineering, Hunan University)
資料名： Dianzi Xianwei Xuebao  (Dianzi Xianwei Xuebao)
巻： 35  号： 5  ページ： 379-385  発行年： 2016年 
JST資料番号： W1469A  ISSN： 1000-6281  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 本論文では、実際の応用の見通しがあり、三段階時効を経た7N01アルミニウム合金に対して、透過型電子顕微鏡観察と力学性能試験を用いて、合金の力学的性質と析出相の微細構造との関係を系統的に研究した。その結果,3段階時効状態を有する7N01アルミニウム合金の降伏強さと引張強さは,直接熱処理のものよりも著しく改善され,伸び率は低下しないことがわかった。透過型電子顕微鏡観察により,ピーク時効状態における合金の主要強化析出相は,Η′相とGPゾーンであることがわかった。また,自然時効で形成された合金元素原子集団にGPゾーンが生成し,それらは人工時効段階で直接Η’相粒子に変換することができた。三段階時効処理の合金の強度は一定の範囲内で自然時効段階で形成されたGPゾーンの数と密接な関係がある。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： GPゾーン ,  引張強さ ,  *微細構造 ,  合金元素 ,  *合金 ,  熱処理 ,  機械的性質 ,  *時効 ,  伸び率 ,  降伏強さ ,  *アルミニウム合金
準シソーラス用語： 人工時効 ,  力学的性質 ,  機械的性能 ,  透過型電子顕微鏡法 , 【Automatic Indexing@JST】

著者キーワード (4件)： 7N01 alloy ,  ageing ,  precipitation ,  strength

分類 (2件)： 機械的性質  (WB02030U) ,  組織的硬化現象  (WB01020C)

タイトルに関連する用語 (6件)： 段階 ,  時効 ,  アルミニウム合金 ,  微細構造 ,  機械的性質 ,  研究