裸のGe-Sb-Seカルコゲン化物ガラスファイバテーパの作製と特性評価【Powered by NICT】

Fabrication and characterization of bare Ge-Sb-Se chalcogenide glass fiber taper

著者 (17件)： Luo Baohua (Laboratory of Infrared Material and Devices, Advanced Technology Research Institute, Ningbo University, Ningbo 315211, China) ,  Luo Baohua (Key Laboratory of Photoelectric Materials and Devices of Zhejiang Province, Ningbo 315211, China) ,  Wang Yingying (Laboratory of Infrared Material and Devices, Advanced Technology Research Institute, Ningbo University, Ningbo 315211, China) ,  Wang Yingying (Key Laboratory of Photoelectric Materials and Devices of Zhejiang Province, Ningbo 315211, China) ,  Sun Ya’nan (Laboratory of Infrared Material and Devices, Advanced Technology Research Institute, Ningbo University, Ningbo 315211, China) ,  Sun Ya’nan (Key Laboratory of Photoelectric Materials and Devices of Zhejiang Province, Ningbo 315211, China) ,  Dai Shixun (Laboratory of Infrared Material and Devices, Advanced Technology Research Institute, Ningbo University, Ningbo 315211, China) ,  Dai Shixun (Key Laboratory of Photoelectric Materials and Devices of Zhejiang Province, Ningbo 315211, China) ,  Yang Peilong (Laboratory of Infrared Material and Devices, Advanced Technology Research Institute, Ningbo University, Ningbo 315211, China) ,  Yang Peilong (Key Laboratory of Photoelectric Materials and Devices of Zhejiang Province, Ningbo 315211, China) ,  Zhang Peiqing (Laboratory of Infrared Material and Devices, Advanced Technology Research Institute, Ningbo University, Ningbo 315211, China) ,  Zhang Peiqing (Key Laboratory of Photoelectric Materials and Devices of Zhejiang Province, Ningbo 315211, China) ,  Wang Xunsi (Laboratory of Infrared Material and Devices, Advanced Technology Research Institute, Ningbo University, Ningbo 315211, China) ,  Wang Xunsi (Key Laboratory of Photoelectric Materials and Devices of Zhejiang Province, Ningbo 315211, China) ,  Chen Feifei (Laboratory of Infrared Material and Devices, Advanced Technology Research Institute, Ningbo University, Ningbo 315211, China) ,  Chen Feifei (Key Laboratory of Photoelectric Materials and Devices of Zhejiang Province, Ningbo 315211, China) ,  Wang Rongping (Centre for Ultrahigh Bandwidth Devices for Optical Systems, Laser Physics Centre, Australian National University, Canberra, ACT 0200, Australia)
資料名： Infrared Physics & Technology  (Infrared Physics & Technology)
巻： 80  ページ： 105-111  発行年： 2017年 
JST資料番号： H0184A  ISSN： 1350-4495  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,直径500μmのGe_15Sb_20Se_65裸のガラス繊維を作製し,次に異なるテーパパラメータを持つ漸減。Ramanとエネルギー分散X線スペクトル(EDS)分析は,ガラスの化学組成のわずかな変化,繊維とテーパファイバは,ガラス構造にほとんど影響しないことを示した。ウエスト径はテーパ長さと速度の増加と共に指数関数的に低下することを見出した,コーン直径2.65μmの高品質のテーパファイバは最適テーパリング条件の下で達成できる。最後に,異なるウエスト長さとテーパ比の下で出力伝送のシミュレーションと実験結果は,透過率は腰長とテーパ比の増加と共に減少することを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： エネルギー散逸 ,  透過率 ,  *カルコゲン化物 ,  指数関数 ,  X線スペクトル ,  ガラス構造 ,  *キャラクタリゼーション ,  *ガラス ,  ガラス繊維 ,  化学組成
準シソーラス用語： 高品質 ,  テーパファイバ , 【Automatic Indexing@JST】

分類 (3件)： 光導波路,光ファイバ,繊維光学  (BD06030H) ,  赤外・遠赤外領域の測光と光検出器  (BD07032W) ,  図形・画像処理一般  (JE04010I)

タイトルに関連する用語 (8件)： Ge ,  Sb ,  Se ,  カルコゲン化物ガラス ,  ファイバ ,  テーパ ,  作製 ,  特性評価