LA_(0.7)SR_(0.3)COO_3の調製とその性能を研究した。【JST・京大機械翻訳】

Synthesis of Three-Dimensionally Ordered Macroporous Perovskite-Type La_(0.7)Sr_(0.3)CoO_3 Catalyst and Its Performance for NO_x Storage Reduction

著者 (5件)： Li Xingang (School of Chemical Engineering and Technology, Tianjin University, Collaborative Innovation Center of Science and Engineering) ,  Bo Ling (School of Chemical Engineering and Technology, Tianjin University, Collaborative Innovation Center of Science and Engineering) ,  Ding Quan (School of Chemical Engineering and Technology, Tianjin University, Collaborative Innovation Center of Science and Engineering) ,  Yan Huizhen (School of Chemical Engineering and Technology, Tianjin University, Collaborative Innovation Center of Science and Engineering) ,  Jin Fengming (School of Chemical Engineering and Technology, Tianjin University, Collaborative Innovation Center of Science and Engineering)
資料名： Huaxue Gongye Yugongcheng  (Huaxue Gongye Yugongcheng)
巻： 33  号： 6  ページ： 1-7  発行年： 2016年 
JST資料番号： C2924A  ISSN： 1004-9533  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 三次元規則化マクロ多孔性LA_(0.7)SR_(0.3)COO_3触媒を,鋳型としてのポリメタクリル酸メチル(PMMA)を鋳型として鋳型法により調製した。Jiao晶自の自己集合法と前駆体濃度は,三次元あるの調製過程において合成試料の構造に大きな影響を及ぼし,その結果,遠心分離法と前駆体溶液濃度が0.3MOL/Lであることが,前駆体合成のための最適条件であることが判明した。X線粉末回折(XRD)と走査型電子顕微鏡(SEM)の結果により、得られた触媒は三次元秩序の大孔GaiTai鉱構造を形成し、水素昇温還元(H_2-TPR)の結果は、この触媒が還元雰囲気中でより高い安定性を有することを示した。この触媒はNO_X貯蔵還元(NSR)反応において良好な触媒性能を示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 自己集合 ,  X線回折 ,  *三次元 ,  TPR【触媒】 ,  前駆体 ,  触媒 ,  遠心分離 ,  走査電子顕微鏡 ,  触媒活性 ,  最適条件
準シソーラス用語： 還元雰囲気 ,  粉末X線回折 ,  マクロポーラス , 【Automatic Indexing@JST】

著者キーワード (5件)： perovskite ,  3DOM ,  NO_x ,  storage and reduction ,  lean-burn

分類 (1件)： 塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (2件)： 調製 ,  研究