多孔性熱硬化性フェノール樹脂の合成反応過程に関する研究【JST・京大機械翻訳】

Study on the synthesis process of multi-phenols modified resole resin

著者 (4件)： Zhao Huanye (East China University of Science and Technology,Key Laboratory of Specially Functional Polymeric Materials and Related Technology of Ministry of Education,School of Materials Science and Engineering) ,  Liu Yujian (East China University of Science and Technology,Key Laboratory of Specially Functional Polymeric Materials and Related Technology of Ministry of Education,School of Materials Science and Engineering) ,  Zhang Yan (East China University of Science and Technology,Key Laboratory of Specially Functional Polymeric Materials and Related Technology of Ministry of Education,School of Materials Science and Engineering) ,  Fang Jun (East China University of Science and Technology,Key Laboratory of Specially Functional Polymeric Materials and Related Technology of Ministry of Education,School of Materials Science and Engineering)
資料名： Reguxing Shuzhi  (Reguxing Shuzhi)
巻： 31  号： 6  ページ： 54-58  発行年： 2016年 
JST資料番号： C2970A  ISSN： 1002-7432  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： FOURIER変換赤外分光法,ゲル浸透クロマトグラフィー,および熱重量分析を用いて,多孔性熱硬化性フェノール樹脂の構造と特性を研究した。結果は以下を示す。反応時間の延長に伴い、多のメチル基指数の変化は比較的に複雑であるが、全体の変化傾向は先に増加し、その後減少し、メチレン指数は次第に増大し、しかも速くは遅く。樹脂の重量平均分子量は327から4038に増加し,分子量分布は1.30から7.11に増加し,180分の反応では,それぞれ,24.4%,37.8%,37.8%であった。最適条件下で,樹脂の熱安定性は最も良く,800°Cでのチャー収率と熱分解温度はそれぞれ%°Cと529.7°Cであった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 分子量分布 ,  *フェノール樹脂 ,  最適条件 ,  ゲル浸透クロマトグラフィー ,  メチレン基 ,  熱安定性 ,  熱重量分析 ,  チャー ,  反応時間 ,  *多孔性
準シソーラス用語： 熱分解温度 ,  重量平均分子量 ,  メチル基 ,  *反応過程 ,  *熱硬化性 , 【Automatic Indexing@JST】

著者キーワード (4件)： multi-phenols ,  phenolic resin ,  synthesis process ,  thermal stability