Co Cr Fe Ni高エントロピー合金系の固溶体島【Powered by NICT】

Solid solution island of the Co-Cr-Fe-Ni high entropy alloy system

著者 (7件)： He Feng (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) ,  Wang Zhijun (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) ,  Wu Qingfeng (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) ,  Niu Sizhe (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) ,  Li Junjie (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) ,  Wang Jincheng (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) ,  Liu C.T. (Center of Advanced Structural Materials, Department of Mechanical and Biomedical Engineering, College of Science and Engineering, City University of Hong Kong, Kowloon, Hong Kong, China)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 131  ページ： 42-46  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 単相等原子CoCrFeNi高エントロピー合金(HEA)は高い引張延性と破壊靭性を有する有望な高エントロピー塩基である。しかしながら,これらの元素の等モル分率が高エントロピーを持つ単一固溶体を得るための必要十分条件ではない。代わりに,計算された相図(CALPHAD)計算と実験的検証の両方の組合せはCoCrFeNi HEA系における単相領域は大きな単相固溶体島に点から拡張できることを示した。本研究の意義は,HEAは高い設計多様性を設計できることである。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 延性 ,  *固溶体 ,  破壊靱性 ,  状態図 ,  単相 ,  *エントロピー ,  引張 ,  モル分率 ,  *高エントロピー合金 ,  CALPHAD法 ,  機械的性質
準シソーラス用語： CALPHAD ,  必要十分条件 , 【Automatic Indexing@JST】

著者キーワード (3件)： 高エントロピー合金 ,  設計 ,  単相

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： CO ,  Cr ,  Fe ,  Ni ,  高エントロピー合金 ,  固溶体